外加硫酸盐对外加剂性能影响.docVIP

外加硫酸盐对外加剂性能影响摘要： 随着高性能混凝土的不断发展，外加剂成为提高混凝土性能必不可少的组份。近年随着外加剂技术的发展发现外加剂的性能受许多因素的影响，其中水泥中硫酸盐含量对外加剂的性能影响很大，特别是聚羧酸系减水剂对此更是敏感。本文通过在试验中外加硫酸盐的方法研究硫酸盐形态及含量对几种减水剂性能的不同影响，结果发现可溶性硫酸盐对所选定外加剂的性能影响非常明显，而石膏(难溶硫酸盐)对这几种外加剂几乎没有什么影响。 关键词： 硫酸盐 聚羧酸 高效减水剂 Abstract: With the development of high performance concrete becoming more and more deeply, admixture becomes necessary to improve the properties of concrete. In recent years, with the development of admixture technology, the properties is influenced by several parameters. Especially the sulfates content in the cement is critical, it seems to be much more sensitive to polycarboxylate superplasticizer. In this work, sulfates are added into the cement—admixture system to evaluate the influence of the sulfates type and content. Results of the study highlight the properties of admixture are strongly influenced by the soluble sulfates while it doesn?t seem to be sensitive to gypsum. Key words: sulfates, polycarboxylate, superplasticizer 中图分类号： P578 文献标识码： A 文章编号： 0.引言 今天，聚羧酸系高效减水剂在混凝土中得到越来越广泛的应用，作为第三代减水剂聚羧酸减水剂有自己独特的优势：①拥有更高的减水率，②能保证混凝土在极低水胶比(＜0.25)下保持较好的工作性。然而，聚羧酸减水剂对于混凝土中的许多成分也是非常敏感的，不仅对水泥的物理、化学性能非常敏感而且骨料甚至搅拌方式对其影响也非常大【1－4】。因此，聚羧酸减水剂在工程应用中也出现了许多问题。 聚羧酸减水剂遇到的这些问题，近年已引起了广泛的关注。其中水泥中的硫酸盐的数量及形态对混凝土减水剂的性能有很大的影响，水泥中的可溶性硫酸盐大部分是在水泥的烧成过程中带入的，加上在粉磨过程中加入的石膏，他们共同提供了水泥早期水化时抑制C3A水化所需的硫酸根离子。C3A的早期水化过程在水泥—外加剂体系中是极为重要的，它极大地影响着水泥对外加剂的吸附，以及水泥浆体的流动性。 本文将针对硫酸盐在水泥－外加剂体系中的作用展开研究。在研究中采用山水集团生产的东岳牌P.I52.5水泥，在较低硫酸盐含量的情况下，通过外加硫酸盐来调整水泥—外加剂体系中硫酸盐的含量，并观察体系中硫酸盐含量对水泥净浆、砂浆以及混凝土性能的影响。 试验 1.1原材料 水泥：山水东岳牌P.I52.5 外加剂：外加剂采用山东华迪建筑科技有限公司生产的PCE(聚羧酸系高效减水剂)、AS(氨基磺酸盐高效减水剂)、BF多基团高效减水剂三种外加剂，掺入时均以有效成份计算。 硫酸盐材料：CaSO4·2H2O、CaSO4·1／2H2O、CaSO4、K2SO4、Na2SO4 1.2试验方法 1.2.1水泥净浆流动度 试验方法按照GB/T8077-2000进行，外加剂掺量分别为PCE 0.2%，AS 0.3%，BF 0.4%，然后掺入水泥中的硫酸盐的量(以SO3计)分别为水泥质量的0.2％，0.4％，0.6％，0.8％，来评价硫酸盐含量及形态对水泥浆体的影响。 1.2.2混凝土试验 试验方法参照GB8076—97中的规定，坍落度按照GBJ80进行测定，分别检测硫酸硫酸盐含量及形态变化对混凝土坍落度的影响。混凝土配合比/㎏,m (水泥) ∶m(砂子) ∶m (石子) ∶m (水)＝1：2：2.55：0.45。外加剂掺量分别为PCE 0.2%，AS 0