某金矿全泥氰化锌粉置换厂工艺流程技术改造实践.docVIP

某金矿全泥氰化锌粉置换厂工艺流程技术改造实践摘要：该矿石属少硫化矿物石英脉含金矿石，金属矿物主要为黄铁矿；脉石矿物主要为石英，其次为长石、方解石、云母等。矿石中的金元素以自然金的形式产出，并且以裂隙金为主，属于易氰化浸出矿石。经过现场工业生产调试结果证明，采用全泥氰化—锌粉置换工艺流程代替浮选处理该矿石是正确的，尾矿品位由0.57g/t降到0.20g/t，金的回收率由82.87%提高到92.16%，提高了企业的经济效益。 关键词：全泥氰化-锌粉置换、浮选、代替、回收率、经济效益 Abstract: The ore is a sulfide mineral quartz vein ore less, metal minerals is mainly pyrite; major gangue mineral is quartz, feldspar, calcite, followed by mica. Of gold in Ores by natural gold in the form of output elements, and fissure gold, is easy to cyanide leaching of ores. After the industrial production debugging results show that, using the all sliming cyanidation - zinc powder replacement process for flotation treatment of the ore is correct, tailing grade from 0.57g/t to 0.20g/t, the gold recovery rate from 82.87% to92.16%, increasing economic benefits of enterprises. Key words: all slime cyanidation - zinc powder replacement; flotation; replace; recovery rate; economic benefit 中图分类号：F407.3文献标识码A 文章编号： 该金矿自1998年建成投产以来，选矿技术人员围绕着如何提高选矿技术指标和经济效益，对选矿工艺流程进行了多次的变更和革新。对工艺技术参数不断进行修正，使之趋于合理。 1.矿石性质 1.1矿物组成及嵌布特征 该矿石的矿物组成比较简单，金属矿物主要为黄铁矿，偶见有方铅矿、黄铜矿、闪锌矿、白铁矿、毒砂。脉石矿物主要是石英，其次为长石，方解石、云母等。 表1-1 金属矿物相对含量结果 黄铁矿，方铅矿，黄铜矿，闪锌矿，白铁矿多呈不规则粒状星散分布，少数呈细脉状、团块状分布，黄铁矿与方铅矿、黄铜矿、白铁矿构成交代结构。其粒度比较细，一般分布在0.074mm以下。 毒砂：呈自形晶和半自形晶粒状星散分布，偶见与黄铁矿构成交代结构，粒度均小于0.074mm。 1.2自然金及其描述 矿石中金元素呈自然金形式存在，表面清洁，呈亮黄色，反射率高，硬度低，粒度粗细不均，多分布在0.074~0.01mm之间。见表1-2。 表1-2自然金粒级相对含量结果 自然金的形态以角粒状、长角粒状为主，次之为尖角粒状、麦粒状，少量的为浑圆粒状、针线状。见表1-3 表1-3自然金形态相对含量结果 自然金的嵌存关系主要与脉石密切，次之与黄铁矿有关，根据嵌布的部位不同可划分为裂隙金、粒间金及包裹金，见表1-4 表1-4自然金嵌存关系相对含量结果 1.3矿石的化学分析 矿石的光谱半定量分析及多元素分析见表1-5、表1-6 表1-5矿石光谱半定量分析结果 2.选矿生产流程对比 2.1该矿原选矿流程是单一浮选工艺流程（一粗二精三扫）。由于矿石中金属矿物嵌布粒度很细，一段磨矿难以达到细粒金属矿石单体解离，造成金属硫化矿物浮选尾矿跑高，使这部分金难以回收，致使尾矿金品位偏高。流程及工艺参数见图2-1，选别指标见表2-1。 图2-1原选矿浮选工艺流程 表2-1 （1998—2008）原选矿厂生产指标结果 产品名称 产率% 品位g/t 回收率% 金精矿 6.98 36.57 82.87 尾矿 92.02 0.57 17.13 原矿 100.00 3.08 100.00 通过矿物工艺学的研究，虽然金属矿物嵌布粒度比较细，但是与脉石矿物界限比较明显。矿石的物质组成比较简单，从矿石的多元素分析结果看，除金、银外，其它有