氯盐对硫酸根离子在混凝土内部扩散性能影响.docVIP

氯盐对硫酸根离子在混凝土内部扩散性能影响摘要：通过单一硫酸盐环境以及氯盐和硫酸盐共同环境中混凝土的浸泡腐蚀试验，测试了不同腐蚀环境中硫酸根离子含量随龄期和氯离子浓度变化而变化的规律，研究腐蚀环境中氯盐的存在及其浓度变化对硫酸根离子在混凝土内部扩散性能的影响。结果表明，氯盐的存在可延缓硫酸根离子在混凝土内部的扩散；氯盐的存在能够降低硫酸根离子含量随时间增长的幅度，且氯离子浓度越大，这种降低作用越明显。 关键词： 混凝土；氯盐；硫酸根离子；扩散性能 The effect of chloride on concrete under sulfate attack Liang Yong-ning1，Huang Jun-yi2，Lin-Xujian1，Ji Tao1 (1. College of Civil Engineering, Fuzhou University, Fuzhou, Fujian 350108, China 2. Fujian Academy of building research, Fuzhou, Fujian, 350025, China) Abstract: The specimens of concrete were immersed into single chloride solution, single sulfate solution and composite solution respectively; the compressive and flexural strength of concrete were tested at different immerse ages, and meanwhile the corrosion products were studied by XRD. The results indicate that the presence of chloride in composite solution can delay the damage of concrete, and the higher the concentration of chloride in composite solution, the more obvious the delayed effect. chloride ions can react with hydration products of concrete and generate hydrated calcium aluminum chloride(3CaO·Al2O3·CaCl2·10H2O), whose expansibility is higher than that of ettringite, becoming the reason of the delayed damage of concrete. Key words: concrete; chloride; sulfate; damage; corrosion products 中图分类号： TU528 文献标识码： A 文章编号： 我国东部有着绵长的海岸线、西北部也存在着大量的盐渍地及盐湖地区，例如青海、新疆、内蒙古。然而，这些海洋环境、盐湖、盐渍地环境中往往富含多种对混凝土结构能够产生侵蚀的离子，如SO42-及Cl-[1]。因此，这些地区的混凝土结构通常在SO42-及Cl-共存的环境中运行，容易产生病害，影响混凝土结构的使用寿命。综合国内外研究现状可以发现，国内外对SO42-、Cl-共同腐蚀效应下的混凝土复合损伤的研究较少，许多方面有待进行进一步的研究及探索。例如在扩散性能方面，对于在硫酸盐单独侵蚀下的混凝土硫酸根离子扩散性能研究比较多[2]- [5]。但对SO42-、Cl-共同腐蚀环境中Cl-的存在及其浓度变化对硫酸根离子在混凝土内部扩散性能影响的机理和规律研究的比较少，尚需作进一步的研究。因此，本文通过试验测试了不同腐蚀环境中硫酸根离子含量随龄期和Cl-浓度变化而变化的规律，研究腐蚀环境中Cl-的存在及其浓度变化对硫酸根离子在混凝土内部扩散性能的影响。 1 试验 1.1 试验材料 水泥采用福建省炼石牌42.5级普通硅酸盐水泥，粗骨料为粒径小于10mm的连续级配碎石，细骨料为闽江河砂，细度模数为2.4。 硫酸钠粉末由天津科贸化学试剂有限公司产，分子式为Na2SO4；氯化钠粉末由上海锦悦化工有限公司生产，分子式为NaCl。 1.2 试验设计 （1）混凝土试件 混凝土试件的成型尺寸为40mm×40mm×160mm，配合比见表1。 表1 混凝土配合比