浅议架空电力线路大容量导线.docVIP

浅议架空电力线路大容量导线[摘要]文章阐述了由耐热铝合金线、退火铝线、成型铝线等导体与碳钢、“Invar”钢、碳纤维-聚合物复合强度材料组合的大容量导线的特点、性能，并提供了经改进后的NRLH（60%IACS）GJ-400/35钢芯耐热铝合金导线的试验结果。为了推广应用和开发新颖的大容量导线，建议：对大容量导线的选择应多方案比较；调研总结已在网运行的耐热铝合金导线线路的设计和运行经验；组织不同学科和行业进行深入研讨。 [关键词]大容量；导线；架空线路 Abstract: The article describes the characteristics and performance of a large-capacity wire composed by conductors of heat-resistant aluminum alloy wire, annealed aluminum wire, molded aluminum wire with composite strength materials of carbon steel, “Invar” steel, carbon fiber – polymer, and provides the test results of the improved NRLH (60% IACS) GJ-400/35 heat-resistant aluminum alloy conductor with steel core. In order to promote and develop the new large-capacity wire, the author suggests that multiple programs proposals should be compared for selecting; the summary of research should be made on the design and operation experience of the heat-resistant aluminum alloy wire line being operated; a in-depth research should be carried out involving various disciplines and industries. Key words: large-capacity; wire; overhead lines 中图分类号：F407.61文献标识码：A 文章编号：2095-2104（2012） 随着电力需求的不断增长，输电线路输送容量不断增大，需要发展大容量导线。导线传输大容量有2种思路：（1）采用耐热铝合金导线或软铝线，提高导线的运行温度；（2）改变导线的结构，采用梯形等股线，提高填充系数，增加导线的载流面积。国际电工委员会标准（IEC-62219）已建议将耐热铝合金线、钢芯软（退火）铝绞线（ACSS）和型线同心绞架空导线作为IEC/TC7项目提出。大容量导线的制造，关键在于材料（导电材料和加强材料）通过不同组合，制造出具有不同特性的组合导线（Compos-ite Conductor）。大容量导线的开发和应用，我国与日本、欧洲、北美等先进工业国相比，有相当大的差距。 上世纪80年代，上海电缆研究所曾开发过58%和60%IACS的耐热铝合金线，但品种和使用少，其线路的设计和运行经验也少；也曾开发过钢芯软（退火）铝绞线和型线同心绞架空导线，但仅作为技术储备。在应用方面，不仅有高温和超高温架空线路设计，亦有配套金具、连接和施工等问题。2020年以前，将是我国电力事业一个超常发展的时期，也是提高输电线路容量，需要发展大容量导线的重要时期，因此了解和研讨大容量导线很有现实意义。 1大容量组合导线的导电材料和加强材料 1.1导电材料 导电材料有耐热铝合金线、硬铝线和软铝线3种，它们可做成圆形或梯形等股线进行绞合。 1.1耐热铝合金线（见表1） 根据耐热等级和强度，耐热铝合金线分为超耐热、特别耐热、耐热和高强度耐热4种，按导电率分有55%，58%，60%IACS等几个档次。在几十年的发展中，尽管牌号甚多，但都属铝-锆合金。随着铝中含锆量的增加，其耐热性提高，但导电率下降。因此需要研究添加其他辅助元素和采取热处理等措施。 目前导电耐热铝合金有以下2种类型： （1）固溶型耐热铝合金。早期的耐热铝合金（如58和60TAL），由于耐热等级较低，且为了满足导电率的要求，一般含锆量不大于0.1%，因此这种线的价格与电工纯铝线相比，增加不多。 （2）固溶析出型耐热铝合金。超耐