多沙水域水轮机防水力破坏措施分析.pdfVIP

38 多沙水域水轮机防水力破坏措施分析 2012.№5 水轮机及水泵 多沙水域水轮机防水力破坏措施分析 梁 兴，李志红 （南昌工程学院，江西 南昌 330099 ） [摘 要] 磨蚀、空蚀是水轮机效率降低及诱发水力机组振动的主要因素之一。本文分析了水轮机水力破坏 的主要原因，总结了常见的抗磨蚀、抗空蚀措施及其在水电站中的应用情况，这对进一步提高我国多泥沙河 流中水电站的运行管理水平，具有重要参考意义 ，同时指出发展新型抗磨蚀材料、采用高新喷涂工艺是防止 水轮机水力破坏的有力措施。 [关键词] 冲刷磨蚀；空蚀；水轮机；涂层；腐蚀 [中图分类号]TK730.5+3 [文献标识码] A [文章编号]1000-3983(2012)05-0038-03 Research on Hydraulic Failure Resistance of Hydraulic Turbine Used in Sediment-laden Waters LIANG Xing ，LI Zhihong (Nanchang Institute of Technology, Nanchang 330099, China) Abstract: The reasons of hydraulic failure in turbine is analyzed, the measures that are used to resist the abrasion and cavitation are summarized, which applications in the hydropower stations are common. It is significant to enhance the operation and management of hydropower stations which work in sediment-laden waters, and it is pointed out that developing new materials and using high-tech coating technology are effective to prevent the destruction of hydraulic power. Key words: abrasion; cavitation; turbine; coating; corrosion 用材选择和抗磨蚀涂层等方面进行讨论，并展望了减 前言 轻水力破坏损失技术的发展趋势。 由冲刷磨蚀以及空蚀等现象所造成的水力破坏 ， 1 多相流诱发的水力破坏现象 对叶片、导水机构、阀门、上冠、底环乃至水工建筑 物等水电站过流部件都有一定的危害。受此影响，我 水轮机水力破坏现象一般被分为两大类：冲刷磨 国现有水电站，特别是黄河、长江流域的水电站几乎