不锈钢刻蚀 【摘要】 本文依据工业生产原理，设计了新的能处理较大面积工件的化学刻蚀装置，研究了实验室条件下对不锈钢进行图纹装饰的方法和工艺。通过上感光材料、感光、刻蚀、上色等工艺实现了不锈钢的图案刻蚀，成功地制作出一批作品。 【关键词】 图纹装饰，不锈钢板，感光材料，刻蚀。 Etching on Stainless Steel Sheet Zhao Libing Chen Peixian Li Jiahang Long Jieming Wang Junxia Liu Chang Zhang Zhijun Liu Xiaofang Lu Yujing Xie Guangbin Lü Xueyi （Class 99, School of Chemistry and Chemical Engineering, Sun Yat-Sen University, Guangzhou 510275, China） Supervisor: Fang Beilong and Chen Liuping 【Abstract】 This paper reported the method and technology for the decorative patterns on stainless steel sheet under the lab’s condition based on the principle of industrial production, and a new apparatus for chemical etching stainless steel sheet of relative large areas is designed. The technical procedures includes painting sensitive material, sensitization, Etching, coloring etc. process. A number of products with various pattern and characters. 【Keywords】 Pattern decoration, Stainless steel sheet, Sensitive material, Etching. 一、引言 不锈钢具有很高的力学强度、硬度、耐磨性、耐蚀性以及易于加工等优良性质，随着其图纹装饰加工工艺的发展和成熟，在各个领域中的应用日益扩大，如在招牌制作、仪器设备表面图文刻印、制造印刷用的金属字板、在机械加工较为困难的薄板或薄片零件（电子线路板、金属网板的小孔以及光栅）等器件上制造出复杂的图形或文字。不锈钢的图纹装饰是通过对不锈钢进行部分刻蚀，获得一定深度的图形或文字，在其上着色，从而达到具有立体感的彩色装饰效果。工业上一般采用FeCl3化学刻蚀和阳极溶解两种方法进行刻蚀[3-6]，该方法具有工艺简单、刻蚀速度快、污染少、经济且效果好等优点。 本文在实验室条件下，根据两种方法的原理进行实验研究，并作改进，对实验产品进行分析比较，找出了合适的实验室生产方法和工艺条件。 二、实验部分 1、原材料、试剂及仪器 不锈钢板，规格：60×60mm，39×120 mm，210×297 mm，800×600mm2、76×56cm2，厚度1~1.5mm。材质：从市场上购得的一般砂光板。 感光胶：二苯甲酮（光敏剂）、不饱和树脂（成膜剂）、有机溶剂。 显影粉，去皮水，焗漆。 刻蚀液配方： FeCl：400～500g/L HPO：20～30g/L HCl：80～120g/L 再生剂（HO）：适量 电解液配方： KCl：10%～18％ HCl：5～10g/L 空气压缩机，恒温槽，自制刻蚀容器，稳定直流电源，电加热炉，电磁搅拌装置等。 2、工艺流程 3、刻蚀工艺 （1）上感光胶 工业上是用喷枪喷涂或150目的尼龙丝网，用上浆器刮涂感光胶在工件表面，但此方法在实验室难以实现。本实验是用天那水按1:3将感光浆稀释，再用丙酮调成极稀浓度，用喷壶喷淋在工件表面。待丙酮挥发完全后，放入烘炉，在80℃下烘30min。 （2）曝光、显影、封边 将制作好图案的黑白胶片平放在感光胶表面，在紫外光灯下曝光2～3min，曝光后马上放入显影液中显影，未感光部分溶解，露出部分不锈钢表面。显影后用清水冲洗，晾干。然后把不需要刻蚀的底面和边沿封好保护。 （3）刻蚀 A) 阳极溶解刻蚀 电解法刻蚀不锈钢电解液对工艺影响较大，要求能在电场作用下对阳极金属产生阳极溶解而不产生钝化膜, 还要有电导率高、流动性好、性能稳定、价格便宜等优点。工业上采用10%～18％的NaCl溶液[7,8]，再根据不同的需要加入NaNO3