6061铝合金焊接试样在大气和潮湿环境下的疲劳寿命研究_英文_姬浩.pdfVIP

下载本文档

6
0
约1.71万字
约 3页
2017-08-17 发布于浙江
举报
版权申诉

6061铝合金焊接试样在大气和潮湿环境下的疲劳寿命研究_英文_姬浩.pdf

1、本文档共3页，可阅读全部内容。
2、原创力文档（book118）网站文档一经付费（服务费），不意味着购买了该文档的版权，仅供个人/单位学习、研究之用，不得用于商业用途，未经授权，严禁复制、发行、汇编、翻译或者网络传播等，侵权必究。
3、本站所有内容均由合作方或网友上传，本站不对文档的完整性、权威性及其观点立场正确性做任何保证或承诺！文档内容仅供研究参考，付费前请自行鉴别。如您付费，意味着您自己接受本站规则且自行承担风险，本站不退款、不进行额外附加服务；查看《如何避免下载的几个坑》。如果您已付费下载过本站文档，您可以点击这里二次下载。
4、如文档侵犯商业秘密、侵犯著作权、侵犯人身权等，请点击“版权申诉”（推荐），也可以打举报电话：400-050-0827(电话支持时间：9:00-18:30)。
5、该文档为VIP文档，如果想要下载，成为VIP会员后，下载免费。
6、成为VIP后，下载本文档将扣除1次下载权益。下载后，不支持退款、换文档。如有疑问请联系我们。
7、成为VIP后，您将拥有八大权益，权益包括：VIP文档下载权益、阅读免打扰、文档格式转换、高级专利检索、专属身份标志、高级客服、多端互通、版权登记。
8、VIP文档为合作方或网友上传，每下载1次，网站将根据用户上传文档的质量评分、类型等，对文档贡献者给予高额补贴、流量扶持。如果你也想贡献VIP文档。上传文档

6061铝合金焊接试样在大气和潮湿环境下的疲劳寿命研究_英文_姬浩

Rare Metal Materials and Engineering Volume 44, Issue 5, May 2015 Online English edition of the Chinese language journal Cite this article as: Rare Metal Materials and Engineering, 2015, 44(5): 1116-1118. ARTICLE Fatigue Life of 6061 Aluminium Alloy Welding Samples both in Atmosphere and Water 1 2 2 Ji Hao , Zhang Chengyu , Qiao Shengru 1 The First Aircraft Institute, Xi’an 710089, China; 2 Northwestern Polytechnical University, Xi’an 710072, China Abstract: 6061-O and 6061-T4 aluminum alloy sheets with 0.04 inch (1.02 mm) nominal thickness are widely used in the aviation industry. After argon arc welding, the sheets were subjected to a solution heat treatment followed by a quenching and tempering treatment (T62 treatment), afterwards fabricated to specimens. The fatigue tests were carried out at 60 Hz, stress ratio of 0.1 both in atmosphere and water at room temperature, and loading direction was perpendicular to welding bead. The fracture morphologies were examined by scanning electron microscopy (SEM). The results show that the fatigue life in water is considerably decreased, and fatigue striation is not so clear compared with that in atmosphere, which might be attributed to the fact that the oxygen content on the fracture surface tested in water after dry treatment is much higher than that in atmosphere. Key words: fatigue life; 6061 aluminum alloy; welding joint; water; atmosphere 6061 aluminum alloy is widely used in the aviation industry. Table 1 Chemical composition of 6061 aluminum alloy (wt%) Although this alloy has a good resistance to corrosion and Mg Si Cu Mn Cr Ti Fe Zn Other total Al good weldability compar