住宅现浇板裂缝成因研究及防治.docVIP

住宅现浇板裂缝成因研究及防治摘要：随着施工技术及施工工艺的提高，传统的钢筋混凝土预制楼板被现浇板所取代，房屋的整体性、抗不均匀性及结构安全性有了显著提高。但随之带来了一些新的问题，例如现浇板的裂缝。作为工程监理，凭着多年的工作经验及对多处住宅现浇板的裂缝的调查研究，从设计、施工、混凝土原材料及成品保护方面分析了现浇板裂缝存在的原因，总结了现浇板裂缝的预防措施及处理办法。 关键词：钢筋混凝土现浇板；裂缝原因；防治技术措施；处理方法 Abstract: with the construction technology and the improvement of construction technology, the traditional reinforced prefabricated concrete floor was replaced by site casting integrated, the integrity of the house, fight not uniformity and structure security has improved. But then brought in some new problems, such as the site casting integrated crack. As project supervision, with many years of work experience and more homes to crack site casting integrated research, from design, construction, concrete raw material and finished product protection the site casting integrated analysis the reason of the existence of the crack, summarizes the crack prevention measures and site casting integrated treatment measures. Keywords:Ferroconcrete cast-in-Place floor; Crack causes; Prevention and control technology measures; Processing method 中图分类号: TU755文献标识码：A文章编号： 1 钢筋混凝土现浇板裂缝原因的分析 通常情况下，现浇板裂缝表现为：不规则、不连贯的表面微裂缝，纵向、横向裂缝以及斜向裂缝。裂缝位置大都出现在暗埋管线的位置上，基本上与板支座负筋相平行或在负筋范围外，很少出现在板面负筋交叉处。究其原因，主要有设计、施工及混凝土原材料、成品保护等方面的原因。 1.1 设计方面 1.1.1 地基的不均匀沉降 在住宅建设中,有一部分的钢筋混凝土现浇板的裂缝，是由于地基不均匀沉降的原因而造成的。设计师对地基情况的不熟悉导致基础设计欠妥出现由不均匀沉降引起的裂缝。 1.1.2 荷载的作用 在住宅建设中，也有少部分钢筋混凝土现浇板的裂缝，是由于荷载作用方面的原因引起的。经验不足的设计人员在进行现浇板的配筋计算过程中，通常只是根据其承载能力来确定配筋量的，而忽略了对板在正常使用阶段由其承受的荷载而引起的挠度及裂缝宽度的验算，由此而引起裂缝的产生。 1.1.3 结构体型突变及未设置必要的伸缩缝 为了提高土地的利用率，某些建筑尺度过长而又未考虑设置伸缩缝，当房屋的自由伸缩达到应设置伸缩缝要求的间距时，就要引起裂缝的产生。 1.1.4 管线敷设位置不合理 在楼房的设计中，随着PVC电线套管的普遍使用、所需的管线直接敷设于现浇板中，而且有时集中于某一处现浇板中的管线多达数根，并且这些管线的直径多为20～30mm，由此就会使该处的现浇板有效面积减少,由于线管和混凝土线胀系数不一致，粘结效果差从而引起现浇板在该处开裂。 1.2 施工质量方面 1）混凝土在施工过程中振捣过度，使粗骨料沉落挤出水分、空气，表面呈现泌水而形成竖向体积缩小沉落，造成表面砂浆层，它比下层混凝土有较大的干缩性能，待水分蒸发后，易形成凝缩裂缝。模板、垫块在浇筑混凝上之前未洒水润透，太过干燥，由于模板吸水量大，引起混凝土的塑性收缩，产生裂缝。 2）混凝土浇筑振捣后，过分抹干压光会使混凝土的细骨料过多地浮到表面，形成含水量很大的水泥浆层，水泥浆中的氢氧化钙与空气中二氧化碳作用生成碳酸钙，引起表面体积碳水化收缩，导致混凝土板表