建筑工程常见裂缝产生及处理措施.docVIP

建筑工程常见裂缝产生及处理措施【摘要】在建筑工程中，裂缝的产生是十分普遍的。有些裂缝影响建筑结构，有的破坏建筑的使用功能，有的只是影响建筑物的外观。为了保证建筑的安全和美观，我们需要了解和研究各种裂缝产生的条件、原因，因势利导地探索出裂缝的处理方法和技术手段，并不断积累实践经验，丰富和完善裂缝的处理措施。本文主要谈谈混凝土建筑工程常见裂缝的产生及处理措施。 【关键词】建筑工程常见裂缝 原因 处理措施 Abstract: in construction works, the cracks are very common. Some cracks in the building structure, and some to undermine the use of the building features only affect the appearance of the building. In order to ensure the safety and aesthetics of the building, we need to understand and study various crack conditions, reasons, to make the best use to explore the processing methods and techniques of the cracks, and continue to gain practical experience, enrich and improve the measures of the cracks. In this paper, talk about common cracks of the concrete construction engineering and treatment measures. Key words: common cracks in the building works because the measures 中图分类号：TU761 文献标识码：A文章编号： 一、混凝土工程中常见裂缝及原因 1、干缩裂缝 干缩裂缝多出现在混凝土养护结束后的一段时间或是混凝土浇筑完毕后的一周左右，水泥浆中水分的蒸发会产生干缩且这种收缩是不可逆的，干缩裂缝的产生主要是由于混凝土内外水分蒸发程度不同而导致变形不同的结果，混凝土受外部条件的影响表面水分损失过快，变形较大，内部湿度变化较小变形较小，较大的表面干缩变形受到混凝土内部约束，产生较大拉应力而产生裂缝。相对湿度越低，水泥浆体干缩越大，干缩裂缝越易产生。干缩裂缝多为表面性的平行线状或网状浅细裂缝，宽度多在0.05——0.2mm之间，大体积混凝土中平面部位多见，较薄的梁板中多沿其短向分布，干缩裂缝通常会影响混凝土的抗渗性，引起钢筋的锈蚀影响混凝土的耐久性在水压力的作用下会产生水力劈裂影响混凝土的承载力等等混凝土干缩主要和混凝土的水灰比、水泥的成分、水泥的用量、集料的性质和用量、外加剂的用量等有关。 2、温度裂缝 温度裂缝多发生在大体积混凝土表面或温差变化较大地区的混凝土结构中，混凝土浇筑后，在硬化过程中，水泥水化产生大量的水化热，由于混凝土的体积较大，大量的水化热聚集在混凝土内部而不易散发，导致内部温度急剧上升，而混凝土表面散热较快，这样就形成了内外的较大温差，较大的温差造成内部与外部热胀冷缩的程度不同，使混凝土表面产生一定的拉应力。当拉应力超过混凝土的抗拉强度极限时，混凝土表面就会产生裂缝。 3、荷载变化引起的裂缝 混凝土桥梁在常规静、动荷载及次生应力下产生的裂缝称荷载裂缝，归纳起来主要有直接应力裂缝、次生应力裂缝两种。直接应力裂缝是指由外荷载引起的直接应力产生的裂缝。此种裂缝产生的原因很多，如设计阶段荷载漏算、内力配筋错误、结构安全系数不够等；施工阶段不按施工图施工，随意在结构上堆码材料机具等，使用阶段超载行驶，受撞击等都可能引起该种裂缝。次应力裂缝是指由外荷载引起的次生应力产生的裂缝。此种裂缝产生的原因有：如设计阶段由于结构物的实际工作状态同常规计算有出入或计算不考虑；计算简图不够精确等。研究表明，受力构件挖孔后，力流将产生绕射现象，在孔洞附近密集，产生巨大的应力集中，因此，若处理不当，在这些结构的转角处或构件形状突变处、受力钢筋截断处容易出现裂缝。 4、地基不均匀沉降产生的裂缝 一般在建筑物下部，由下往上发展，呈“八”字、倒“八”字、水平及竖缝。当长条形的建筑物中部沉降过大，则在房屋两端由下往上形成正“八”字缝，且首先在窗对角突破；反之，当两端沉降过大，则形成的两端由下往上的倒“八”字缝，也首先在窗