提高蒸硒回转窑使用寿命的措施.pdfVIP

技术改造 提高蒸硒回转窑使用寿命的措施 侯琼英 , 彭德安 (大冶有色金属有限公司 稀贵金属厂 , 湖北 黄石 435005) [摘 　要] 针对蒸硒回转窑负压波动较大 、窑尾冒酸水 、温度控制不稳定 、窑尾下料箱腐蚀严重 、使用寿命短等问题 , 对蒸硒回转窑采取一系列改造和维护保养措施 ,取得较好的效果 。 [ 关键词] 蒸硒回转窑 ; 窑寿 ; 温度 ; 负压 ; 密封 ; 同心度 ; 燃烧器 ( ) [ 中图分类号] TF80612 　　　[文献标识码] B 　　　[文章编号] 1003 - 8884 2007 05 - 0033 - 04 Measure of Prolonging Life of Rotary Selenium Kiln HOU Qiongying , PEN G Dean (RareNoble Metals Plant ,Daye Nonferrous Metals Co . Ltd . ,Huangshi 435005 ,China) Abstract : This paper describes a series of improvement and maintenance measures for rotary selenium kiln . They are used to solve many problems ,for instance ,negative pressure fluctuates badly inside the kiln ,waste acid water flows off from the rear of the kiln ,temperature is kept difficultly ,blanking bin at the rear of kiln is corroded seriously ,and the service life of the kiln is short . The result indicates that these improvement mea sures are successful . Key words : rotary selenium kiln ; life of rotary selenium kiln ; temperature ; negative pressure ; sealing ; con centricity ; burner 　　稀贵金属厂一车间目前有两台蒸硒回转窑 ,分 图 1 为生产流程示意图。 别投建于 2001 年和 2002 年 ,用于铜电解阳极泥的 硫酸化焙烧 ,设计使用寿命为 6～9 个月 , 日处理阳 极泥量为每台蒸硒窑 15 t 。窑筒体直径为 1 m ,窑 筒体长度为 11 m ,焙烧的阳极泥在窑筒体内采用螺 旋传送 ,阳极泥中的水分焙烧后经过四级吸收塔 、通 过真空泵 、再经环保处理 、最后由尾气风机排出。窑 体分三段燃烧室 ,每段燃烧室设一台燃烧器 ,每台燃 烧器独立工作 ,分别独立控制每段燃烧室的温度 。 铜电解阳极泥先用浓硫酸浆化 ,再通过圆盘加料机 图 1 　阳极泥焙烧生产工艺流程图 加到窑筒体的头部 ,边焙烧边由螺旋传送至窑尾 ,经 Fig. 1 　Process flow diagram of the anode slime roasting 窑尾下料箱集中后定时放出 ,转入下一道生产工序 。 经过几年的摸索和对蒸硒窑的不断改进 ,