紧固件生产过程（Fastener production process）.docVIP

紧固件生产过程（Fastener production process） The forming method of forging at the top of the bar or wire diameter at room temperature. Cold heading is used in the manufacture of bolts, nuts, nails, rivets and steel parts. Forging stock material can be copper, aluminum, carbon steel, alloy steel, stainless steel and titanium alloy, the material rate of up to 80 ~ 90%. Cold heading in special cold heading machine, to achieve continuous, multi station, automatic production. In order to complete cutting, upsetting, accumulation, forming, chamfering, rubbing, necking and cutting processes in cold heading machine. The production efficiency is high, up to 300 / cent above, the maximum diameter of 48 mm cold forging workpiece. Heading bolt process schematic diagram for the typical process of heading bolt. Multi station nut automatic cold heading machine for multi station nut automatic cold heading machine. Bar feed mechanism automatically sent by a certain length, cutting off their bodies cut into blanks, and then transmitted by the clamp mechanism in order to accumulate pressing and punching station for forming. Cold upsetting refers to the raw material at room temperature for stamping, hot upsetting refers to the raw material after heating for stamping, specific uses no special requirements, generally require cold, because such a surface finish, material composition would be more closely, there is a large workpiece used the hot upsetting process. Forging the head, also called hot pier, the head of heating, extrusion molding; Most of the pier, because it can save material. According to the size and tonnage of forging machine bolt diameter, can be used cold pier or hot upsetting technology. Six head bolts special or special small batch is turning into milling after. Small batch can be used die threading, thread lathe, milling milling method. Method of rolling machine, screw rolling machine rolling wire used in mass production, high efficiency. Because the bolt forming method of dra