Effect of processing way and aging treatment on properties and microstructures of 7B04 aluminum alloy LI Nian-kui(李念奎)1 2 1 , LÜ Xin-yu( 吕新宇) , CUI Jian-zhong(崔建忠) 1. Key Laboratory of Electromagnetic Processing of Materials, Ministry of Education, Northeastern University, Shenyang 110004, China; 2. Northeastern Light Alloy Co. Ltd, Harbin 150060, China Received 22 October 2007; accepted 14 December 2007 Abstract: The influence of forging and aging treatment on mechanical properties and microstructure of large size prestretched thick plate of 7B04 aluminium alloy was investigated through tensile test, corrosion test, transmission electronic microcopy(TEM) and energy dispersive spectrum(EDS) analysis. The results show that the properties of plate performed extra forging (FSR technology) are much higher than those of plate without forging (CSR technology). T7451 temper is preferred to resisting corrosion than T65 1 temper due to a wide PFZ and discontinuous grain boundary precipitates. Key words: 7B04 aluminum alloy; processing way; aging; microstructure; exfoliation corrosion; stress corrosion tensile properties, corrosive properties and 1 Introduction microstructures of this large size prestrethed thick plate processed by CSR and FSR technologies, respectively, The aerospace industry is constantly striving