高炉封炉（Blast furnace sealing）.docVIP

高炉封炉（Blast furnace sealing） Practice of sealing blast furnace and air recovery in No. 6 blast furnace of Anyang Iron Steel Works Angang No. 6 380m3 Blast Furnace began to seal the furnace for 5 days and 970 minutes at 0:00 on December 2, 2002. Many measures have been taken to seal the furnace and restore air, and the operation has been well done and good results have been achieved. It took only three days to arrive from the storm. Keywords sealing and air cleaning operation 1. overview Anyang Steel No. 6 blast furnace of 380m3 in December 2, 2002 to 7 at 16:10 on the furnace top equipment repair packet. The repair work lasted 5 days and 970 minutes, and good results were achieved in sealing furnace and recovering air. No serious accidents such as taphole opening and tuyere burning were found during the process of air blowing. It took three days to arrive from the storm. 2. furnace operation Hugh two days before the wind wash ratio of fluorite and fluorite ore batch furnace, as 9kg / T, Hugh wind 16 hours before the addition of fluorite increased to 18kg / T. 1 days in advance to stop oxygen enrichment, pipeline safety check, and raise the furnace temperature, reduce the slag basicity. Before the wind, [Si] control at about 1%, thoroughly check the cooling equipment leakage. As far as possible, the wind shall be operated with full air pressure, and when the temperature of the raw gas reaches 260 degrees, the operation of reducing air or stopping the gas can be carried out, but it is necessary to ensure that the air supply is released to the hearth. The burden of burden shall be shown in table 1. The ratio is 80% sintering, 20% Hainan, furnace grade 57%, total ore volume 154.2t, total coke quantity 172.8t, total iron quantity 93.5t, charging volume 383m3, load 0.89. 6 hours (1 days, 18 hours), the next break off material, the process of iron mouth angle and iron mouth channel gradually expanded, and strive to more slag iron. When the wind is finished, the material li