煤粉预热对其燃烧反应动力学参数的影响 杨永昌， 王 恒， 赵俊东 （北京科技大学机械工程学院，北京，100083） 摘要：本文采用非等温热重技术对煤粉预热前后燃烧反应动力学参数进行研究。试验使用微机差热天平、升温速率为20℃/min、升温范围从室温到1100℃，分别对预热前后煤粉进行热重分析。采用积分法(Coats—Redfern方程)计算得到动力学参数活化能E和指前因子A。结果表明：煤粉预热后燃烧反应动力学参数发生了变化，改善煤粉的 文献标识码：A Impact of pulverized Coal Preheating on its Combustion Kinetics Parameters YANG Yong-chang, WANG Heng, ZHAO Jun Dong (School of Mechanical Engineering, University of Science Technology Beijing, Beijing 100083, China) Abstract: The paper studied the combustion kinetics of pulverized coal before and after preheating by the non-isothermal thermogravimetry analysis (TGA). The microcomputer differential thermal balance was used in the test, and the TGA of pulverized coal before and after preheating was conducted respectively when the temperature ranged from room temperature to 1100℃ with a heating rate of 20℃/min. The activation energy E and pre-exponential factor A were calculated using the Coats-Redfern integral. The results show that the coal kinetic parameters have been changed, and the ignition of preheated coal powder has been improved, which makes the coal ignition temperature lower and the burning speed faster. Key words: PC combustion；thermogravimetry analysis；reaction kinetics；activation energy 0 前言 高炉炼铁喷吹煤粉已成为钢铁企业节焦增产、合理利用煤炭资源、减少环境污染、降低生产成本 工业分析 元素分析 成分 FCad Vad Aad Mad Cad Had Oad Nad Sad 质量％ 75.89 12.35 10.77 0.99 79.94 3.67 2.98 1.31 0.34 HCT-1型微机差热天平。主要性能：加热温度范围：室温～1150℃，调温速度：0.1～20℃/min，差热量程：±10～±1000μv，热重量程：1～200mg。实验条件：煤样实验样品均为20mg，升温速率为20℃/min，最终加热温度为1100℃ 。 2 试验研究方法 2.1燃烧反应动力学分析 本文采用Coats-Refern积分法进行研究。 根据质量作用定律及Arrhenius定律，非等温热重实验的反应速率方程可以表示如下 ： （1） 煤样的燃烧转化率α可以根据热失重 （TG）曲线求出： （2） 其中，t为时间，s；T为温度，K；为升温速率，℃/min；A为指前因子，s-1；E为反应的活化能，kJ/mol；R为气体常数，其值为 8.31410-3kJ/(mol·K )；、和分别代表反应开始前、反应t时刻和反应结束时样品的质量，mg；n为反应级数。 煤的燃烧反应通常被描述为一级反应[3]，由（1）式积分，得 （3） 根据Doyle关系（取前2项近似），积分移相得： （4） 令,在本文中反应温度区及E值而言，可以近似看做常数，令，，，则有，。