干湿法熄焦对焦炭强度影响及对比分析.docVIP

干湿法熄焦对焦炭强度影响的对比分析 魏玉玲，徐文胜，胡建军 (济南钢铁集团总公司技术监督处，山东 济南 250101) 摘　要：通过测定焦炭强度和水分,对干法熄焦和湿法熄焦对焦炭质量进行了对比分析。结果表明:熄焦炭提高了成熟度，减少了微裂纹的产生，改善了内部结构，其抗碎强度M40比湿熄焦炭提高了6%，焦炭水分降低5%。关键词：干法熄焦；湿法熄焦；抗碎强度；焦炭水分中图分类号：TQ522.16　　 文献标识码：B　　 文章编号：1004-4620(2002)05-0029-02 Comparison Analyses of Influences of Coke Dry Quenching?and Coke Water Quenching on Coke Strength WEI Yu-ling, XU Wen-sheng, HU Jian-jun (Ｔhe Technical Supervision Department of Jinan Iron and Steel Group，Jinan 250101，China) Abstract：The influences of coke dry quenching and coke water quenching on coke strength are compared and analyzed through determining the coke strength and water content.The results show that the maturity of dry quenched coke is increased,the crack initiation is decreased,the internal structure is ameliorated,the broken strength M40 that compares with it of water quenched coke is increased by 6% and the water content in the coke is reduced by 5%.Key words：coke dry quenching;coke water quenching;broken strength;water?content in the coke 1 前? 言 　　干法熄焦即焦炭从炭化室被推出后，不是用水淋熄，而是用惰性气体或非助燃性气体吹熄。　焦炭系统的主要流程为：焦炉——焦灌车——提升机——加焦装置——干熄炉——排焦装置——皮带——中间焦仓。湿法熄焦即将从炭化室推出的焦炭迅速送至熄焦塔下用水喷洒80～120s，控水1min，然后将焦炭卸至焦台。　济南钢铁集团总公司(简称济钢)自1999年3月采用干法熄焦以来，对减少熄焦烟尘、回收利用红焦余热、改善大气环境起到了积极作用，焦炭机械强度得到了很大提高，为高炉炼铁提供了优质原料。 2 干法熄焦对焦炭水分的影响 　　焦炭水分是冶金焦炭的重要物理性能指标，它的高低和稳定性对高炉操作起到重要作用。湿焦与干焦水分测定的结果如表1、表2所示。 表1 未采用干法熄焦前的焦炭水分％ 1 2 3 4 5 6 7 8 9 10 平均 波动范围 5.1 4.3 5.0 4.3 4.4 5.1 5.2 4.7 4.7 4.3 　 　 4.5 6.5 2.8 5.5 5.4 5.3 4.2 4.4 4.2 5.8 4.7 2.8～5.8 4.8 5.0 3.9 4.6 4.6 4.6 4.4 4.2 4.6 5.3 　 　 ??表2 干熄焦正常运行后干焦水分％ 1 2 3 4 5 6 7 8 9 10 平均 波动范围 0 0 0.2 0 0 0.2 0.2 0.4 0.2 0.2 　 　 0 0 0.2 0 0.2 0.4 0.2 0.2 0 0.2 0.17 0.2～0.8 0 0.2 0 0.2 0.2 0.2 0.2 0.2 0.2 0.2 　 　 　　? 从表1看出：湿法熄焦焦炭水分在2.8%～5.8%左右，湿法熄焦容易使水分波动，对高炉用焦炭以重量计算时将影响上料量变化，容易引起炉况波动。??? 由表2可知：干法熄焦,焦炭水分在0.2%～0.8%左右,波动很小,有利于稳定高炉操作。 3 干法熄焦对焦炭机械强度的影响 　　焦炭的机械强度是指焦炭的抗碎强度（M40）和耐磨强度（M10）。　湿熄焦炭与干熄焦炭的强度测试结果分别列入表3、表4。 表3 未采取干法熄焦前的焦炭机械强度％ 项目 1 2 3 4 5 6 7 8 9 10 平均 波动范围 M40 78 76.6 76.8 77.0 78.6 77.2 77