特殊玻璃纤维套管规格.docx

丙烯酸酯玻璃纤维套管KL-2740Polyurethanes fiberglass sleeving丙烯酸酯玻璃纤维软管是由无碱玻璃纤维编织成坯管，再涂以丙烯酸酯乳胶经加热烘干而成的B级绝缘软管。具有可靠的耐热性，良好的电性能，较好的的柔软性与弹性，以及耐苯、耐油等特性，适用于电机、电器、仪器、仪表、无线电、电视机及空调、风扇、洗衣机等家用电器的布线绝缘与机械保护。外观：表面光洁，端部整齐。耐油：软管在105±2℃的变压器油中浸24小时，漆膜不应与玻璃丝管脱开或产生开裂，允许漆管颜色变深。耐苯:漆管在常温甲苯液体中浸4小时，漆膜不发粘贴或脱落。Acrylic glass fiber hose is woven E-glass fiber blank tube, coated with acrylic latex is made by heating and drying of the Class B insulation hose. Reliable heat resistance, good electrical properties, good softness and flexibility, and resistance to benzene, oil and other properties, for electrical, electronics, instruments, meters, radio, TV and air-conditioning, fans, washing machines, etc. appliance wiring insulation and mechanical protection.Appearance: smooth surface, the ends neatly.Oil: hose at 105 ± 2 ℃ transformer oil immersed for 24 hours, the film should not be torn off or cracking glass tube, allowing the paint tube darker.Resistance to benzene: toluene liquid paint tube immersed at room temperature 4 hours, the film is not made ??paste or off.内径壁厚标称（mm）偏差（±）最小最大0.3、0.5、0.8 ±0.100.20 0.50 1.0、1.5 ±0.150.20 0.75 2.0、2.5 ±0.200.20 0.75 3.0、3.5、4.0、5.0、6.0±0.250.20 0.75 7.0、8.0±0.500.300.759.0、10.0、12.0、14.0、16.0、18.0 ±0.500.40 0.90 20.0、23.0、25.0、27.0 ±0.500.40 1.00技术参数性能指标击穿电压（KV）常态时≥2.5 受潮后≥1.5 缠绕后≥1.2 弹性温度：20±5摄氏度，相对湿度：65±5%，软管在规定棒径上缠绕1小时。漆膜不应与玻璃丝管脱开或产生开裂。软管在-10-15摄氏度的环境下处理2小时，立即在规定棒径上缠绕。漆膜不应与玻璃丝管脱开或产生开裂。软管在130±2摄氏度的环境下处理24小时，然后于20±2摄氏度的室温下在规定棒径上缠绕。外侧漆膜不应与玻璃丝管脱开或产生开裂。耐油软管在105±2摄氏度的变压器油中浸24小时漆膜不应与玻璃丝管脱开或产生开裂，允许漆管颜色变深。耐苯软管在常温甲苯液中浸4小时漆膜不发粘或脱落。认可标准︰JB/T 8151.3―1999聚氨酯玻璃纤维套管KL-2741Polyurethanes fiberglass sleeving聚氨酯玻璃纤维软管系采用无碱玻璃纤维编织成管，并涂以改性聚氨酯树脂经加热烘干而成的F级绝缘漆管。具有可靠的耐热性，良好的电性能，较好的柔软性与弹性。适用于作F级电机、电器及仪表、无线电、家用电器等装置的布线绝缘与机械保护。。Polyurethanes fiberglass sleeving, woven as sleeving by non-alkali fiberglass and coated with polyurethanes in high temperature. It has excellent dielectric, and softness feature, widely used in the class HN motor, household electrical appliances, heatingequipment, th