聚合松香季戊四醇酯合成过程中催化剂的初步研究 化学与材料工程学院 08应用化学（本科） 2008063533 曾成财 指导老师：吴粦华 摘要 本实验以聚合松香和季戊四醇为原料，选取不同的无机盐催化剂（如ZnO、MgO、Ce(SO4)2等），在一定温度范围内（本实验为220-240℃）合成聚合松香季戊四醇酯。通过对聚合松香的酸值以及酯化之后聚合松香季戊四醇酯酸值的测定，进而计算酯化率，可知反应进行的程度。对催化剂的选用、Polymerization pentaerythritol ester synthesis catalyst in the process of the preliminary research College of Chemistry Mchem Science, Longyan University 2008063533 zeng chengcai Instructor WU Lin-hua Abstract: In the present study polymerization rosin and pentaerythritol as raw materials, the selection of different inorganic salt catalysts (such as ZnO, MgO, Ce (SO4) 2, etc), in certain temperature range (this experiment for 220-240 ℃) synthetic polymer pentaerythritol ester. Through to the polymerization of rosin acid value, esterification after polymerization pentaerythritol ester the determination of acid value, and then calculating esterification rate, it can be seen that the extent of the response. The choice of catalysts, reaction time and reaction temperature on synthesis of polymerization pentaerythritol ester influence of the research, determine product acid value, get different esterification rate, be orthogonal concludes that synthetic polymer pentaerythritol ester of suitable conditions. Keywords:?Polymerization rosin pentaerythritol Polymerization pentaerythritol ester Acid value Esterification rate 1 引言 1.1松香 1.1.1松香概括 松香由于其结构上的特点使其具有许多优良性能,如防腐、防潮、绝缘、粘合、乳化、软化等,因此广泛应用于肥皂、造纸、油漆、塑料、电气、医药、农药、印染、化工等领域[1] 。但是,由于松香结构本身还存在一些不足,如在溶剂中的结晶倾向性大,易被大气中的氧所氧化,软化点偏低,易于和清漆中的重金属盐发生反应,因而限制了它在另外一些工业部门中的应用。我国松香资源丰富,脂松香产量居世界首位,因此,提高松香的使用价值,对于我国的国民经济有着很重要的现实意义。通常可以利用松香树脂酸结构中的双键和羧基这两个化学反应活性中心进行松香改性,制备松香衍生物。 1.1.2 松香的物理性质 表1-1松香的物理性质 项目 指标 外观 黄色脆性固体 色泽 淡黄色至红色 溶解性 不溶于水,溶于有机溶剂 软化点( ℃) 72～80 相对密度 1. 070～1. 085 平均热容(20～245 ℃, kcal/ (kg·℃) ) 0. 54 熔解热(kcal/ kg) 15. 8 熔化松香膨胀系数( ℃) 0. 000 55 热值(kcal/ kg) 9074～9171 沸点( ℃/ 5 mmHg) 250 导热系数(kcal/ (m·h·℃) ) 0. 11 雾状粉尘燃点( ℃) 130 闪点( ℃) 216 爆炸下限(g/ m3) 12. 6 1.2聚合松香概括 聚合松