MLA在银的赋存状态研究中的应用 王俊萍， （北京矿冶研究总院 矿物加工科学与技术国家重点实验室，北京10） 摘 要：结果表明：矿石中53.42%、44.26%及2.31%。这些银矿物呈0.020mm以下的细粒或微细粒嵌布于云母类矿物中，少部分包裹于白云石、石英或重晶石中产出。可见，磨矿时单体解离不充分以及选矿时分选白云石，都将导致部分银损失于尾矿中。 关键词：MLAPLICATION OF MLA IN THE STUDY OF SILVER OCCURRENCE WANG Jun-ping WU Hui-min WANG Ling (State Key Laboratory of Mineral Processing of China, Beijing General Research Institute of Mining and Metallurgy, Beijing 102628, China) ABSTRACT: The silver grade of an associated silver deposit is 89.2g/t. In order to determine the silver occurrence state, the systemic research is carried out with instruments such as optical microscope and large advanced MLA. The result shows that the silver in the ore mainly exists in three kinds independent minerals; argentite, naumannite and aguilarite respectively; and the distribution ratio of the silver in those minerals are 53.42%, 44.26% and 2.31% respectively; and the silver mineral grains which are small than 0.020mm are mostly wrapped up by mica minerals and only a small part of the silver mineral grains are wrapped up by dolomite, quartz or barite. So，insufficient liberation of silver minerals and the rejection of dolomite by reverse flotation will cause silver losing in the tail. KEY WORDS: silver; occurrence; MLA; 湖北宜昌某伴生银矿中Ag的品位为[1-2]。镜下初检表明，矿石中银矿物具有种类多、嵌布特征复杂，嵌布粒度细微等特点。传统的 MLA是目前世界上最先进的工艺矿物学参数自动定量分析测试系统[3-5]。运用MLA进行了详细的 采用-0.074mm的分析样进行矿石的化学分析见表。 表化学分析结果 Table Chemical analysis results of the ore /% 元 素 V Fe C S Cu Pb 含 量，% 2.870 5.750 1.580 0.033 0.008 元 素 Ba Ti P SiO2 Al2O3 含 量，% 0.390 0.230 0.160 39.88 9.370 元 素 CaO O Na2O K2O Ag 含 量，% 8.780 0.080 4.220 89.20 ：Ag的单位为 g/t。 ： g/t for Ag。 结合化学分析、化学物相分析、X-射线衍射为表 矿石的矿物组成及含量 Table Mineral composition of run-of-mine ore / % 矿物名称 云母类矿物 黄铁矿 褐铁矿 黄铜矿 闪锌矿 方铅矿 含 量，% 2.710 0.540 0.100 0.010 0.010 矿物名称 重晶石 白云石 石英 长石 方解石 磷灰石 含 量，% 37.10 21.36 10.11 1.080 0.890 矿物名称 碳质 其它 含 量，% 0.660 3 MLA检测矿石中银矿物的嵌布特征 据初检结果，该矿石中的银矿物具有颗粒细微、嵌布特征复杂、光学特征不明显等特点，用传统的光学显微镜进行矿物定量将费时费力、无法