硫化钠沉淀法回收镍镁液中的镍-有色金属科学与工程.DOCVIP

硫化沉淀法回收镍镁液中的镍 钟 斌，曾清全 （江西江钨钴业有限公司，中国 赣州341000) 摘要：以Na2S为沉淀剂，沉淀钴湿法冶金系统中产生的镍镁液，回收其中的镍。通过单因素实验，考察了Na2S用量、沉淀pH、反应温度、反应时间和陈化时间对Ni、Mg沉淀率和过滤性能的影响。实验结果表明，最优的工艺条件为Na2S用量为沉镍理论用量的1.3倍，反应过程pH控制在4.5左右，反应温度60 ℃，反应时间2 h，陈化时间1 h。在最优的工艺条件下，Ni、Mg的沉淀率分别为99%和11%，过滤性能良好，无穿滤现象。 关键词：硫化沉淀法；硫化钠；沉淀率；过滤性能 Nickel Was Recovered from Nickel-Magnesium Solution by Sulfuration Deposition Method ZHONG Bin,ZENG Qing-quan (Jiangxi JiangWu?Cobalt Industry Ltd,Ganzhou 341000,China） Abstract: Nickel was recovered from Nickel-magnesium solution. The effects of Consumption of Na2S, the precipitation of pH, the reaction temperature, the reaction time and the aging time on precipitation rates of Ni,Mg and performance of filtration with single factor experiment. The results show that the precipitation rates of Ni, Mg are 99%,11%, respectively, The precipitations have?good filtration performance and no?wear?filter?phenomenon. Under the optimum conditions including the content of Na2S was 1.3?times the?amount?of the?theory, the precipitation of pH about 4.5, the reaction temperature of 60 ℃, the reaction time of 2 h and the aging time of 1 h. Key words: sulfuration deposition method; sodium sulfide; precipitation?rate; filtration performance 0 引 言 在钴湿法冶金系统中，存在大量镍镁液。从镍镁液中回收有价金属镍不仅有较高的经济价值，且能大大降低污水处理的负担。目前，从镍镁液中回收镍的方法主要有溶剂萃取法、氢氧化物沉淀法和硫化物沉淀法。由于镍镁液中的镍浓度不高（约0.5 g/L），采用溶剂萃取法不仅一次性投入大，且运行成本高，回报不高，不宜实施。 与氢氧化物沉淀相比，硫化物沉淀法具有诸多优点，如：硫化物沉淀性能更好，反应速率快，对金属的选择性沉淀效果好，金属硫化物的溶解度更低，等[1-2]。 硫化物沉淀法在金属的分离和富集[3-9]及废水处理方面[10-12]有着广泛的应用，相关报道也较多。工业上常用的硫化剂有H2S、Na2S、NaHS、Na2S2O3等含硫化合物[13]。 本文以Na2S为沉淀剂，对镍镁液的沉淀工艺进行了研究。考察了Na2S用量、沉淀pH、反应温度、反应时间和陈化时间对Ni、Mg沉淀率和过滤性能的影响。 1 实 验 1.1 实验原料及设备 实验原料：镍镁液，其主要成分为：Ni2+(0.58 g/L)，Mg2+(0.33 g/L)，pH=4.5、Na2S·9H2O(AR)、H2SO4溶液、NaOH溶液。 实验设备：恒温水浴锅，电动搅拌器，烧杯，分液漏斗，量筒，移液管，电位-pH计，温度计，等。 1.2 实验与分析方法 取一定体积的镍镁液于烧杯中，置于恒温水浴锅中升温并搅拌，取一定质量的Na2S?9H2O晶体并配置成质量分数为10%的Na2S?9H2O溶液于分液漏斗中，在一定温度