常用的钣金材料（Commonly used sheet metal material）.docVIP

常用的钣金材料（Commonly used sheet metal material） Common sheet metal material I. galvanized steel Galvanized steel mainly in two categories: 1. Electro galvanized sheet (EG) 2, hot dip galvanized sheet (GI). Table 1: comparison of galvanized sheet with hot dip galvanized sheet Galvanized sheet (EG/SECC) hot dip galvanized plate (GI) Base metal, cold rolled annealed steel plate, cold rolled hard steel plate Pretreatment; electroplating; hot plating It is difficult to plating zinc and difficult to plating Zinc coating on the surface of the coating is of steel. The surface is smooth, without zinc, the zinc layer is solidified, and the zinc flower or zinc free flower can be used The coating is pure zinc, the outer layer is pure zinc, and the inner layer is iron zinc alloy The mechanical properties and the same motherboard after annealing, a hardening of soft material; The processing performance is similar to that of base metal. The formability is good, it can withstand simple processing and complex processing can not be competent The material thickness is common and the material thickness is 0.6~1.5mm The corrosion resistance of the coating is thin, poor thick coating, good can Jianai fingerprint coating The price is cheap Two. Stainless steel Stainless acid resisting steel, which is corrosive to atmosphere, acid, alkali, salt and other medium. To achieve stainless steel corrosion resistance, chromium (Cr) amount of not less than 13%; in addition, can be added nickel (Ni) or molybdenum (Mo), etc. to increase the effect. As alloy species There are many kinds and different contents. Stainless steel features: good corrosion resistance, good brightness, high strength, certain elasticity, expensive. Characteristics of stainless steel: 1, ferritic stainless steel: its high Cr content, with good and high temperature oxidation resistance. 2, austenitic stainless steel: typical brands such as /Cr18Ni9, /Cr18Ni9T1, no magnetism, good corrosion resistance, temperature strength and high