铝青铜结合剂磨具的研究探究.doc

2016届毕业生 毕业论文 题 目: 院系名称：材料科学与工程 专业班级： 学生姓名： 学 号： 指导教师： 何方 教师职称： 教授 201年 5 月 日 700℃，压强3.5MPa，最高温度保温五分钟。由Cu77Al6Fe6Ti5Ni6制备的结合剂试样强度和硬度都符合金属结合剂的力学性能要求，加入金刚石后硬度虽然有下降，但是强度和硬度都在性能要求范围之内。 关键词：铝青铜 热压烧结 抗弯强度 洛氏硬度 Title： Research on aluminum bronze bonded abrasive tool Abstract This topic is to prepare an aluminum bronze bond formulation through consulting literature, and to explore its sintering process. The sintering method was adopted in the experiment.Firstly, the influence of the content of Al on the performance of the sample was studied in two yuan Cu-Al, and the sintering process was selected, including sintering temperature, pressure, holding time and so on through consulting literature,Two yuan Cu-Al formula and sintering process were determined according to the performance requirements of the metal bond and by testing the performance of the test specimens.Then join the Fe, Ti, Ni elements in turn,each element is added to the three different temperatures for sintering, and the corresponding pressure is changed.then, the mechanical properties such as hardness and bending strength were measured, and the formula and sintering process were obtained. The results of experiments and performance tests show that each element is sintered at different temperatures and different concentrations,the best content ratio is choosed according to the hardness,the sintering temperature is 700 degrees C, the pressure is 3.5MPa, the maximum temperature of heat preservation holds for five minutes.The strength and hardness of the bond asmples prepared by Cu77Al6Fe6Ti5Ni6 are consistent with mechanical properties of the metal bond,although the hardness of diamond is decreased, the strength and hardness are all within the range of performance requirements. Keywords: Aluminum Bronze Hot-pressing Sintering Bending Strength Rockwell Hardness 目录 1 引言 1 1.1铝青铜概述 1 1.2铝青铜结合剂磨具 1 1.2.1金属结合剂金刚石磨具的分类 1 1.2.2铝