扫描电压幅值调控循环方向的NiOx薄膜电阻开关特性.PDFVIP

See discussions, stats, and author profiles for this publication at: /publication/276487677 Reversed bipolar resistive switching behaviors modulated by scanning voltage amplitude in polycrystalline NiO x films Article · Januar 2015 DOI: 10.1360/SSPMA2015-00007 CITATIONS READS 0 42 5 authors, including: Xiao an Qiu Southwest Universit in Chongqing 42 PUBLICATIONS 262 CITATIONS SEE PROFILE Some of the authors of this publication are also working on these related projects: Resistive swithching memor View project Magnetic fluids and nanopartiles View project All content following this page was uploaded b Xiao an Qiu on 04 Ma 2016. The user has requested enhancement of the downloaded file. 中国科学: 物理学 力学 天文学 2015 年 第45 卷 第5 期: 057701 《中国科学》杂志社 SCIENTIA SINICA Physica, Mechanica Astronomica SCIENCE CHINA PRESS 论 文 扫描电压幅值调控循环方向的NiOx 薄膜电阻开关 特性 霍进迁, 张祎扬, 朱华星, 王瑞雪, 邱晓燕* 西南大学物理科学与技术学院, 重庆 400715 *联系人, E-mail: qxy2001@ 收稿日期: 2015-01-06; 接受日期: 2015-03-01; 网络出版日期: 2015-03-20 国家自然科学基金(批准号:、重庆市自然科学基金(编号: cstc2014jcyjA40029)和中央高校基本科研业务费专项资金(编号: XDJK2014B043)资助项目 摘要 本文利用射频磁控溅射方法在优化制备条件下沉积制备了沿[200]晶向择优取向的多晶 NiOx 薄膜. Ag/NiOx/Pt 电容器结构的电流- 电压曲线具有典型的双极性电阻开关特性, 但循环方向与扫描电压幅值有关: 当最大扫描电压小于2 V 时, 电流- 电压曲线沿逆时针方向循环, 高/低电阻值比大于 50, 可稳定维持超过50 个循环周期. 当最大扫描电压增大到2 V, 电流- 电压曲线变为沿顺时针方向循环, 高/低电阻值比大于 10, 可 稳定维持超过120 个循环周期. 电流- 电压曲线循环方向随扫描电压幅值的改变揭示了其不同的电阻开关物理 机制: 低扫描电压下逆时针循环电阻开关特性主要归因于电场作用下氧离子定向漂移导致氧空位形成的导电 细丝通道周期性地导通和截断; 当最大扫描电压增加到2 V 时, 银离子扩散进入NiOx 薄膜与定向漂移的氧离 子发生氧化/还原反应合成/分解AgOx , 使得薄膜导电性周期性地增大和减小, 从而使得NiOx 薄膜具