强风区750kV复合绝缘子伞裙破坏机制分析研究.PDFVIP

34 6 Vol.34 No.6 Feb.25, 2014 2014 2 25 Proceedings of the CSEE ©2014 Chin.Soc.for Elec.Eng. 947 DOI 10.13334/j.0258-8013.pcsee.2014.06.017 0258-8013 (2014) 06-0947-08 TM85 750 kV ( 518055) Analysis on Fracture Failure Mechanism of 750 kV Composite Insulator Sheds Utilized in a Storm-hit Region ZHU Zhengyi, JIA Zhidong, MA Guoxiang, WANG Xilin, GUAN Zhicheng (Graduate School in Shenzhen, Tsinghua University, Shenzhen 518055, Guangdong Province, China) ABSTRACT: This paper provided a explicit explanation of 0 composite insulator sheds fatigue failure mechanism in storm-wind region. Through the work of field research on the sheds fatigue failure, experimental study on rubber material fatigue crack, simulation with fluid-solid interaction of sheds and the static deformation of the special shed structure, it’s found that large amount of composite insulator faced with fatigue fracture problem on the 750 kV EHV transmission lines across particular storm-wind region with the mean wind velocity over 30 m/s in Xinjiang, the most serious case of 750 kV single insulator was that the loss of valid creepage distance reached 20.4%. The test results show that the insulator silicon rubber had bad performance on anti-fatigue property. The fluid 29 induced oscillation of insulator sheds in storm wind brought 750 kV 28~42 m/s about the stress concentration problem at the root areathe application of cycled stress pro