冷却速率对β成核剂聚丙烯结晶行为的影响.docVIP

 毕业设计（论文） 题 目β成核剂聚丙烯结晶行为的影响 学生姓名： 系 别： 材料工程系 专 业： 高分子材料 学 号： 班 级： T933-3 指导老师：任伊锦 摘 要 关键词：聚丙烯；β晶型成核剂；改性；结晶；性能 Abstract The use of differential scanning calorimetry cooling rate on B nucleating agent modified polypropylene (PP) crystallization behavior. Lower the cooling rateSlow, high temperature longer the residence time, the PP is higher crystal content B, PP higher impact strength. Cooling rate of 5 e / m in time, PP polymorph B in massScore of 8b 1 P / o; cooling rate of 20 a / m in time, B crystal mass fraction of 72 0} / 0; and when the sample to a very rapid cooling, B crystal content ofCb B crystal of PP slow crystallization rate of the A-type crystal PP, only at a higher temperature range of isothermal crystallization, B crystal was faster crystallization rate of the PP in the crystal AType PPa Therefore, under normal processing conditions polymorph B content is less. Keywords: Polypropylene B cooling rate crystallization nucleating agent 目录 第1章 概 论 2 1.1 课题背景及意义 2 1.2 本课题及相关领域的国内外现状及发展 2 1.2.1 聚丙烯的结构与性能 2 1.2.2 聚丙烯添加剂改性的发展现状[2] 3 1.2.3聚丙烯成核剂 4 1.3 主要研究内容 5 第二章 实验方法 6 2.1 实验仪器 6 2.2 实验材料 6 2.2.1 聚丙烯 6 2.2.2 β晶型成核剂 6 2.3 实验方法 7 2.3.1 样品制备 7 2.3.2 性能测试 9 第三章 实验结果及分析 11 3.1 力学性能测试 11 3.1.1 拉伸性能测试结果及分析 11 3.1.2 抗冲击性能 11 3.2 DSC（差示扫描量热法） 12 3.3 X射线衍射 14 3.4 偏光显微镜观测照片 14 第四章 结论 16 致谢 17 参考文献 18 第1章 概 论 1.1 课题背景及意义 随着人们在生活方面需求增大与科学技术的发展，许多生产简单、成本低廉又有很好性能的材料被应用于产品的生产，其中，高分子材料由其良好的性能与高产量正逐步成为主流的原材料，聚丙烯（PP）在五大通用塑料中总产量位居第三，仅次于PE和PVC，也是第二大合成树脂。与其它通用塑料相比，其具有较好的综合性能：无毒性，相对密度小，加工性能与力学性能优良，屈服强度、拉伸强度及弹性模量均较高，电绝缘性好，介电率较小，耐应力龟裂性及耐化学药品性也很出色，且易于加工，热变形温度高等。 但PP也有缺点，由于PP是典型的结晶性高聚物，内部存在着很大的球晶，球晶颗粒较大，使得其脆化温度高，这使得PP 具有成型收缩率高、缺口冲击强度低、低温冲击性能较差、高温刚性不足和韧性差等缺点。由于球晶之间有明显的界面，在界面处易产生应力集中，限制了其使用范围的扩展。因此，PP球晶尺寸的微细化，则可以在很大程度上克服这