混凝土桥梁裂缝成因和治理.docVIP

混凝土桥梁裂缝成因和治理 　　摘要：随着我国交通基础建设的发展，各地兴建了大量的混凝土桥梁。在桥梁建造和使用过程中，由于混凝土裂缝而影响工程质量甚至造成桥梁坍塌的事例屡见不鲜。混凝±开裂可以说是“常发病”和“多发病”，严重影响了桥梁的使用性能，也经常困扰着桥梁工程技术人员。要想控制桥梁混凝土裂缝的产生，就必须了解其成因。 其实只要采取一定的措施是可以克服和控制的，本文就桥梁在建造和使用中的常见病及多发病“裂缝”，进行一些探讨。 关键词：混凝土桥梁裂缝；成因；治理措施 Abstract: With the development of transport infrastructure, built around a large number of concrete bridges. In bridge construction and use of the process, and affect the quality of the project concrete cracks caused by collapsed bridges and even examples are common. Coagulation ± cracking can be said to be “normal incidence” and “disease” seriously affect the performance of the bridge, the bridge is often plagued by engineering and technical personnel. To control the bridge concrete cracks, it is necessary to understand its causes. In fact, as long as the take certain measures can be overcome and control, this paper bridges in the construction and use of common diseases and frequently-occurring disease, “crack”, carried out some research. Keywords: concrete bridge cracks; cause; management measures 中图分类号：U445.47 文献标识码:A 桥梁混凝土裂缝种类及其成因 混凝土结构裂缝的成因复杂、繁多，有时多种因素互相影响，但每一条裂缝均有其产生的一种或几种主要因素。混凝土桥梁裂缝的种类，就其产生的原因，大致可划分如下几种： (一)、荷载引起的裂缝 混凝土桥梁在静、动荷载及次应力下产生的裂缝称荷载裂缝，主要有直接裂缝、次应力裂缝两种。直接应力裂缝是指外荷载引起的直接应力产生的裂缝；次应力裂缝是指由外荷载引起的次生应力产生裂缝。 （二）、温度变化引起的裂缝 混凝土具有热胀冷缩性质，当外部环境或内部温度发生变化，混凝土将发生变形，若变形遭到约束，则在结构内将产生应力，当应力超过混凝土抗拉强度时即产生温度裂缝。在某些大跨径桥梁中，温度应力可以达到甚至超出荷载应力。温度裂缝区别其他裂缝最主要特性是将随温度变化而扩张或合拢。引起温度变化主要因素有：年温差、日照、骤然降温、 水化热、蒸汽养护或冬季施工措施不当等。 （三）、收缩引起的裂缝 在实际工程中，混凝土因收缩所引起的裂缝是最常见的。在混凝土收缩种类中，塑性收缩和缩水收缩（干缩）是发生混凝土体积变形的主要原因，另外还有自生收缩和炭化收缩。研究表明，影响混凝土收缩裂缝的主要因素有：水泥品种、标号及用量、骨料品种、水灰比、外掺剂、养护方法、外界环境、振捣方式及时间。 （四）、地基变形引起的裂缝 由于基础竖向不均匀沉降或水平方向位移，使结构中产生附加应力，超出混凝土结构的抗拉能力，导致结构开裂。基础不均匀沉降的主要原因有：地质勘察精度不够、试验资料不准；地基地质差异太大；结构荷载差异太大；结构基础类型差别太大；地基冻胀；桥梁基础基于滑坡体、溶洞或活动断层等不良地质时，可能造成不均匀沉降。 （五）、钢筋锈蚀引起的裂缝 要防止钢筋锈蚀，设计时应根据规范要求控制裂缝宽度、采用足够的保护层厚度（当然保护层亦不能太厚，否则构件有效高度减小，受力时将加大裂缝宽度）；施工时应控制混凝土的水灰比，加强振捣，保证混凝土的密实性，防止氧气侵入，同时严格控制含氯盐的外加剂用量，沿海地区或其它存在腐蚀性强的空气、地下水地区尤其应慎重。 （六）、冻