论混凝土气泡成因研究和控制技术 　　摘要：随着时代的不断进步，混凝土已全面成为建筑工程中不可或缺的施工材料，混凝土在任何建筑工程中都具有举足轻重的作用。随着混凝土的广泛应用，在其运用过程中难免会出现这样或那样的问题，其中混凝土气泡就是比较突出的问题之一。基于此，本文以《论混凝土气泡成因分析与控制技术》为题，从混凝土气泡的物理特性，气泡稳定性，气泡排出机理，振捣影响，混凝土塌落度对气泡的影响，混凝土气泡的控制措施等几方面进行了分析和探讨；最后对全文进行了总结。 关键词：混凝土气泡；成因分析；控制技术 Abstract: along with the advance of age, an integral part of concrete has become a comprehensive building engineering construction materials, concrete plays an important role in any construction project. With the widely application of the concrete in its use in the process of the hard to avoid can appear this or that problem, in which concrete bubble is one of the prominent problems. Based on this, this article takes the theory of concrete bubbles cause analysis and control technology “, from the physical properties of concrete bubble, bubble, bubble discharge mechanism of the vibrating influence, concrete slump effect on the bubble, bubble of concrete control measures and so on several aspects has carried on the analysis and discussion; Finally, the full text is summarized. Keywords: concrete bubbles; Cause analysis; The control technology 中图分类号：TV331 文献标识码：A 科学技术的不断发展，混凝土工业技术也在不断进步，这就给新时期背景下的建筑企业带来了更多发展的机遇，然而在带来机遇的同时也面临着严峻的挑战。由于混凝土在建筑工程中的广泛应用，就难免存在这样或那样的质量病害，因此，作为新时期背景下的建筑企业应认真分析混凝土应用过程中出现的问题，并针对性地提出相应的解决措施，这样才能提高建筑企业自身的经济效益和社会效益，从而提高自身的核心竞争力，实现企业的升级和转型。 一、混凝土气泡的物理特性 混凝土中的气泡没有顺利的聚集在模板边缘和排出是造成混凝土表面气泡出现的主要原因。在进行混凝土振捣之前会出现大量的气泡，这是由于混凝土在拌合、运输、下料时带来的空气泡而造成的，同时减水剂和引气剂中也会出现一定量的气泡，且单纯水溶液中的气泡，其液膜极为薄弱，极易发生破灭。混凝土浆液中的气泡其液膜一旦粘附大量的固体颗粒，就会产生变化，从而由单纯的液膜转变成固复合液膜，进而液膜的厚度也会增加，弹性也会加强，也令气泡的稳定性得到了极大的增强。利用振捣能直接将一些气泡排出，使一些气泡产生位移，同时大量的单独气泡由于液膜的阻隔，但是在振捣机械作用下，可能会出现粘附情况，致使两泡合而为一，这样经多次作用后就会出现大量大尺度气泡。因而，气泡液膜的稳定性跟大气泡的出现及振捣影响均有着密切关联。 二、气泡稳定性分析 （一）减水剂引入气泡 由于气泡位于水泥颗粒之间，所以减水剂引入的气泡在同等电性斥力作用下会让水泥颗粒分散，进而加强水泥颗粒间的滑动，这能起到有效的减水作用。这类气泡通常都是形状不一、大小不均，还不稳定。振捣的进行会让单独的气泡相互聚合，最终将会形成混凝土气泡。通常又将减水剂中的气泡称为介稳气泡，这是由于水剂中的气泡介于稳定与不稳定之间。 减水剂自身和拌制时会产生一些有害气泡，为了消除这些有害气泡，通常采取的方法是引入具有消泡功能的大分子单体组分，其能有效抑制气泡集合。 （二）引气剂引入气泡 使用引气剂会产生大量的小气泡，这些气泡还是均匀