连续热镀锌机组锌液温度的精确控制.pdfVIP

连续热镀锌机组锌液温度的精确控制 ·1 · 连续热镀锌机组锌液温度的精确控制 张 军 钱洪卫 杨建国 林传华 孟宪陆 （宝山钢铁股份有限公司冷轧厂, 上海 200941 ） 摘 要 锌液温度的控制直接影响到连续热镀锌机组锌锅内锌渣的产生量和锌层中抑制层的成分及结构,进而影响 到热镀锌产品的表面质量。对影响连续热镀锌机组锌液温度精确控制的因素进行了系统分析,通过改进带钢入锌锅 温度的控制,锌液温度的检控精度和锌锅加锌的精确控制，优化锌锅辊预热温度控制等方法, 实现锌液温度的精确控 制。 关键词 热镀锌，锌液温度，锌锅 Accurate Control of Liquid Zinc Temperature in Zinc Pot of Hot-dip Galvanizing Line Zhang Jun, Qian Hongwei, Yang Jianguo, Lin Chuanhua, Meng Xianlu (Cold Rolling Plant, Baoshan Iron Steel Co., Ltd., Shanghai 200941, China) Abstract The liquid zinc temperature control will affect the formation of zinc dross in zinc pot and the composition and phase structure in hibiting layer of the product in CGL line. It will further a ffect the product s surface quality. Finally it will affect the surface qulity of the product. The ralated factors affected the presicion control for liquid zinc temperature were analyzed. The control method for strip temperature at the entrance of zinc pot, the detection accuracy and control method for liquid zinc temperature, the presicion control method for adding zinc ingots and the management mothod for zinc pot roll temperature and so on were improved and optimized, which will be lead to the precision control of liquid zinc temperature. Key words hot dip galvanizing, liquid zinc temperature, zinc pot 1 引言 热浸镀锌过程是把退火处理后的带钢浸入到熔融的锌液（或锌合金液）中,在带钢表面形成纯锌和锌合 金层，同时带钢浸入锌液后，表面一部分Fe 将溶解到锌液中并与锌液中Zn 和Al 等元素的发生反应,形成各 种金属间化合物（即锌渣）。其中锌液温度的精确控制是此过程的关键工艺要求，一方面，锌液温度直接影 响到纯锌层厚度和锌合金层中抑制层的厚度及相结构,进而影响到热镀锌产品质量；另一方面，锌液温度波 动会导致锌液Fe 元素饱和度变化，当锌液Fe 元素过饱和时，多余的Fe 元素便会以锌渣的形式析出，且锌 渣析出为不可逆反应，因此，锌液温度波动会极大增加锌液中锌渣等夹杂物的发生量，从而影响到热镀锌机 组正常的生产组织及热镀锌产品质量。 此前,热镀锌机组未将锌液温度的精确控制作为重点工艺参数加以重视，普遍存在锌液温度波动较大的 现象，直接导致带钢锌层表面质量不稳定以及锌锅内锌渣