磁屏蔽用高磁导率电磁纯铁研究与开发.pdfVIP

磁屏蔽用高磁导率电磁纯铁研究与开发 ·1 · 磁屏蔽用高磁导率电磁纯铁研究与开发 苗 晓 王新宇 胡志强 （山西太钢不锈钢股份有限公司，山西太原 030003 ） 摘 要 开发磁屏蔽纯铁材料新品要满足更高磁性能要求，通过研究化学成分、磁性热处理工艺对晶粒大小和磁性 能的影响，提出了合适的铝含量和磁性热处理温度，实验室成功开发了磁屏蔽用高磁导率电磁纯铁，为工业化生产 开发提供了技术储备。 关键词 磁屏蔽，高磁导率电磁纯铁，研究开发 Research and Development of High Permeability Magnetic Iron for Magnetic Shielding Miao Xiao, Wang Xinyu, Hu Zhiqiang (Shanxi Taigang Stainless Steel Co., Ltd., Taiyuan 030003, China) Abstract New magnetic iron for magnetic shielding needs to meet higher magnetic requirements. Research about effects of chemical composition and magnetic heat treatment on grain size and magnetic properties was carried out. The appropriate aluminum content and magnetic heat treatment temperature were proposed. A high permeability magnetic iron for magnetic shielding was successfully developed in laboratory. Technical reserve was made for mass production. Key words magnetic shielding, high permeability magnetic, research and development 电磁纯铁具有磁感高和磁导率高的特点，相对于铍莫合金，更具有成本低、加工性好、磁性能稳定的特 点。电磁纯铁材料一般加工成封闭型外罩，屏蔽内部磁场源对外界环境的影响，或屏蔽外部环境的磁场对内 部环境或设备仪器的影响，主要用于 MRI 、CT 室、超导发电、电导蓄电等强磁场屏蔽，又如电镜室、电信 设备保护、磁浮列车等方面的弱磁场屏蔽等。 普通电磁纯铁制做大型 CT 屏蔽室需 20 t，开发高性能产品可减少纯铁材料，从而降低磁屏蔽制造成本。 1 技术要求 [1] 高磁导率电磁纯铁性能要求 ： （1）在直流磁场下有高磁感（B 和 B ）、高磁导率（μ和 μ ）、矫顽力（H ）低，退磁性好等，其中弱 s m c 磁场屏蔽要求磁导率高，强磁场屏蔽要求 B 值高； （2 ）加工性良好，满足冲片性、切削、焊接、弯曲成形等不同用途，对弱磁场屏蔽材料要求强度、韧性 和疲劳强度等性能； 苗晓（1979—），男，山东济南人，工程师，从事电工材料工艺技术开发工作。Email ：miaoxiao@ ，Tel ·2 · 第十届中国钢铁年会暨第六届宝钢学术年会论文集 （3 ）金相上要求晶粒粗大，夹杂物含量低且粗化。 拟定要研究的品种为超高磁导率材料，高磁导率、高磁感（特别是低弱磁场）和极低的矫顽力。该产品