不同预处理后麦草组分变化和溶解性能.docVIP

不同预处理后麦草组分变化和溶解性能 　　摘要：研究采用乙二胺、氢氧化钠和硫酸等对麦草进行预处理，分析预处理后麦草的组分变化，并通过X射线衍射对麦草秸秆纤维结晶度的变化进行表征。结果表明，先碱后酸预处理后麦草秸秆纤维的结晶度上升最大。麦草经过预处理后可以溶解在氢氧化钠/硫脲/尿素/水的溶液中，通过对比几种预处理麦草的溶解性能，表明经过先碱后酸预处理后的麦草在氢氧化钠/硫脲/尿素/水的溶液中溶解性能最好。 关键词：麦草；预处理；组分；溶解性能 中图分类号：X712 文献标识码：A 文章编号：0439-8114（2014）01-0033-05 Changes of Components and Dissolution Performance of Wheat Straw after Pretreated with Different Methods YU Ji，YE Ju-di，LI Xiao-bao，ZHAI Shu-jin，SU Meng，YAN Wei，HONG Jian-guo （School of Chemical Engineering， Nanjing Forestry University，Nanjing 210037， China） Abstract： Wheat straw was pretreated in solution of sodium hydroxide， sulphuric acid and 1，2-ethylenediamine. The changes of components and structure of different solution were investigated. The change of crystallinity was characterized by X-ray diffraction. Results showed that wheat straw pretreated in solution of sodium hydroxide-sulphuric acid had the most decrease of crystallinity. Pretreated wheat straw can dissolve in NaOH/urea/thiourea aqueous solution. The dissolving property of wheat straw pretreated was compared. Results showed that wheat straw pretreated in solution of sodium hydroxide-sulphuric acid had the best ability of dissolution. Key words： wheat straw； pretreatment； components； dissolution performance 收稿日期：2013-05-10 基金项目：国家公益性行业（林业）科研专项（201204803）；江苏高校优势学科建设工程资助项目 作者简介：虞 霁（1987-），男，江苏丹阳人，在读硕士研究生，研究方向为废弃物处理与资源化利用，（电话电子信箱） yixuan_yu1127@；通讯作者，洪建国，男，教授，博士生导师，主要从事废弃物资源化利用研究，（电子信箱）hjgnj@。 作为自然界中含量丰富的可再生资源，木质纤维的研究和应用长期以来受到研究者广泛的关注。木质纤维主要由纤维素、半纤维素和木质素三部分组成。然而，由于分子间与分子内氢键的大量存在，并且具有晶区和非晶区共存的复杂结构，木质纤维很难溶于水和普通的有机溶剂，这大大限制了木质纤维的工业应用[1]。氢氧化钠/硫脲/尿素/水溶液体系被认为是纤维素的良好溶剂，具有溶解性能稳定和溶剂易回收的优点，因此，可以将氢氧化钠/硫脲/尿素/水溶液体系应用于木质纤维的溶解上[2，3]。但是，由于木质纤维的复杂结构，使得纤维素、半纤维素、木质素之间的连接很难被打破，不易被溶剂所触及，因此，需要在溶解之前进行一定的预处理。木质纤维的预处理方法主要有物理法、化学法和生物法。物理法主要是机械粉碎，可通过切、碾、磨等工艺使生物质原料的粒度变小，增加和试剂接触的表面积，除此之外，还包括高能电子辐射处理、微波和超声波处理、蒸汽爆破技术等[4]。化学法主要包括氢氧化钠溶液润胀、稀酸预处理、液氨预处理等[5]。生物法是利用分解木质素的微生物除去木质素以解除其对纤维素的包裹作用，能耗低，操作简单，不污染环境，但其处理周期长，效率不高[6]。因此