关于混凝土膨胀剂和补偿收缩混凝土问题探究.doc

关于混凝土膨胀剂和补偿收缩混凝土问题探究 　　摘要：普通混凝土是用途极广的建筑材料，由于它的极限延伸率较低，在干缩、徐变、温度等作用下易引起开裂，导致混凝土工程渗漏、钢筋锈蚀，影响使用功能和使用寿命。从混凝土的原材料角度考虑，膨胀剂的合理使用是解决问题的关键之一。本文简述了混凝土膨胀剂，分析了膨胀剂的补偿收缩混凝土的配制和使用限制，并提出正确适当的使用混凝土膨胀剂应注意的问题和收缩混凝土裂缝问题的解决措施，供设计、施工和混凝土搅拌站的技术人员参考。 关键词：混凝土；膨胀剂；收缩混凝土； Abstract: ordinary concrete is a very useful building materials, because of its lower limit elongation, in under the action of dry shrinkage, creep, temperature, etc is easy cause craze, leading to concrete engineering, reinforcement corrosion, leakage, affect the use function and service life. Think in terms of the raw materials of concrete, the reasonable use of expansive agent is one of the key to solve the problem. This article describes the concrete expansion agent, this paper analyzes the compensation shrinkage concrete expansion agent preparation and use of the limit, and puts forward appropriate right problems that should be paid attention to the use of concrete expansion agent and shrinkage of concrete cracks in the solution of the problem, for the design, construction and concrete mixing plant technical staff reference. Key words: reinforced concrete; Expansive agent; Shrinkage of concrete; 中图分类号：TU528.042文献标识码：A文章编号：2095-2104(2013) 一、混凝土膨胀剂 （一）混凝土膨胀剂及其分类 膨胀剂是在砂浆和混凝土中能通过化学反应产生膨胀的外加剂。混凝土膨胀剂的主要功能是补偿混凝土硬化过程中产生的干缩和冷缩。混凝土膨胀剂有以下类型： 1、硫铝酸钙类 与水和水泥通过水化反应而生成的钙矾石混凝土膨胀剂。如明矾石膨胀剂，PPT、UEA、FS、AEA等。 2、氧化钙类 与水和水泥通过水化反应而生成的氢氧化钙混凝土膨胀剂。如石灰膨胀剂。 3、硫铝酸钙-氧化钙类 与水和水泥通过水化反应而生成的钙矾石和氢氧化钙的混凝土膨胀剂。如CEA。 （二）混凝土膨胀剂作用原理 在自由条件下，将膨胀剂掺入混凝土中，使其与水泥产生水化反应，能产生一定量的膨胀。在限制条件下，使膨胀能力转变为压应力，相当于提高混凝土的抗拉强度，改善了内部应力状态，从而推迟收缩的产生，较好地防止和减少收缩裂缝的出现。 （三）混凝土膨胀剂的适用范围 1、补偿收缩混凝土：地下、水中、海中、隧道等构筑物，大体积混凝土（除大坝外），配筋路面合板、屋面与浴室厕所防水、构建补强、渗漏修补、预应力钢筋混凝土、回填槽等。 2、填充用膨胀混凝土：结构后浇缝、隧道堵头、钢筋与隧道之间的填充等。 3、填充用膨胀砂浆：机械设备的底座灌浆、地脚螺旋的固定、梁柱接头、构建补强、加固。 4、自应力混凝土：仅用于常温下使用的自应力钢筋混凝土压力管。 5、混凝土膨胀剂的适用还应特别注意： 含硫铝酸钙类、硫铝酸钙－氧化钙类膨胀剂配制的膨胀混凝土（砂浆）不得用于长期环境温度为80℃以上的工程。 含氧化钙类膨胀剂配制的膨胀混凝土（砂浆）不得用于海水或有侵蚀性水的工程。 掺膨胀剂的混凝土只适用于钢筋混凝土工程和填充性混凝土工程。掺膨胀剂的大体积混凝土，其内部最高