SUS304亚稳态奥氏体不锈钢马氏体转变量与变形-中国科技论文在线.PDFVIP

中国科技论文在线 SUS304 亚稳态奥氏体不锈钢马氏体转变量 # 与变形模式的关系研究 李细锋，叶丽燕，陈军* 5 （上海交通大学模具CAD 国家工程研究中心，上海 200030 ） 摘要：本文通过单向拉伸实验，分析了拉伸速率对SUS304 亚稳态奥氏体不锈钢马氏体转变 量的影响，速率小于0.005/s 时，随着速率的减小，马氏体转变量明显增多，大于0.005/s 时， 马氏体转变量减少但变化不大。基于十字件拉深成形实验，研究了不同应力状态下马氏体转 变量随应变路径的变化规律，两压一拉应力状态下马氏体转变量最多，单拉和平面应变次之， 10 双拉应力状态下最少。 关键词：SUS304 亚稳态奥氏体不锈钢；十字件；马氏体转变量；应变；应力状态 中图分类号：TG386.4 Study on the relation between deformation modes and 15 martensite volume fraction of SUS304 metastable austenitic stainless steel LI Xifeng, YE Liyan, CHEN Jun (National Engineering Research Center of Die Mold CAD, Shanghai Jiao Tong University, Shanghai 200030) 20 Abstract: Based on tensile tests, the effect of tensile strain rate on martensite volume fraction was investigated. The martensite volume fraction increases obviously when the strain rate is lower than 0.005/s. However, when the value is higher than 0.005/s, the martensite volume fraction fewly changes. Based on Cross-die drawing, the relationship between marteniste volume fraction and strain path under different stress states was studied. The more strain causes a higher martensite 25 volume fraction. The amount of martensite under two compressive stress and a tensile state is the highest followed by uniaxial tension and plane strain. Biaxial tension stress state results in the least one. K