唐钢酸洗破鳞机的工艺参数优化.pdfVIP

唐钢酸洗破鳞机的工艺参数优化 ·1 · 唐钢酸洗破鳞机的工艺参数优化 王学慧 （河北钢铁技术研究总院，河北石家庄 052000 ） 摘 要 唐钢冷轧厂的破鳞机长时间不能正常的投入使用，严重影响了酸洗的产品质量、增加了酸耗，通过对破鳞 机进行大量的研究，在破鳞机张力、循环水、设备、管理等方面进行改进和调整，摸索出一套适合本厂破鳞机的工 艺参数，使该设备能正常的投入使用，提高产品质量，达到了预期的目的。 关键词 酸洗，破鳞机，工艺参数，优化 Optimization on Processing Parameters of Tang Steel’s Picking Scale Breaker Equipment Wang Xuehui (Hebei General Research Institute of Iron and Steel Technology, Shijiazhuang Hebei 052000, China) Abstract Ti was not work on scale breaker equipment of Tang Steel cold rolling plate Co., Ltd. long time. Product quality of picking was serious influence and Increase HCL consume. Ti was researched of a lot to scale breaker equipment ,Ti was improved and adjusted at tension and circulating water and equipments and manage of scale breaker equipment, and find out one set processing parameters suitable of scale breaker equipment, this equipments can working and raise product quality of picking, expect purpose was carry out. Key words picking, scale breaker equipment, processing parameters, optimization 1 引言 唐钢酸洗车间的破鳞机设备由于种种原因一直不能正常运行，破鳞机的作用不能发挥，对产品质量产生 了严重的影响，通过分析破鳞机工作的影响因素，并对这些因素进行有效的改进和调整优化破鳞机的工艺参 数。使带钢的延伸率达到了 1.5%以上，破鳞机基本上可以能正常投入使用，达到了改善酸轧原料的板形、 降低酸耗、降低挤干辊消耗量、使切边顺畅降低工人劳动强度的目的。 2 设备简介 破鳞机包括一个刚性钢结构，架装有2 个上预弯辊箱、2 个下预弯辊盒、一个防横弯辊箱、一个快速打 开机构、一个换箱机构、换箱小车、辊箱旋转装置、湿式氧化铁皮收集系统。最大张力451.5kN ，最大延伸 率 3.0% 。破鳞机具有两个功能：第一是通过拉伸纠正带钢的板形；第二是使带钢两面的氧化铁皮产生均匀 的裂解、松动，从而使酸洗更加有效。 3 问题分析 在酸洗生产线，影响破鳞机正常投入的因素关键有几个方面，而这几个方面也是优化破鳞机参数的主要 王学慧，男，硕士，高级工程师，从事材料研发，wxhtshlg@163.com ·2 · 第十届中国钢铁年会暨第六届宝钢学术年会论文集 解决方向。 3.1 张力 （1）一号酸洗生产线破鳞机在使用过程中有失张的情况发生，尤其是厚度大于3.0mm 的厚规格带钢更 容易失张，因为在运行厚规格的原料时，需要的张力要比运行薄规格的原料大，当带钢焊缝过破鳞机时破鳞 机的工作辊箱要停止工作打开，下辊箱下降以减少焊缝对破鳞机工作辊的冲击，保护辊面不被破坏，当焊缝 通过破鳞机后，下辊箱