原创力文档Study on Hydrogen Permeation in DP and QP Grades of AHSS underCathodic Charging and Simulated Service论文.pdfVIP
- 1、本文档共9页，可阅读全部内容。
- 2、原创力文档（book118）网站文档一经付费（服务费），不意味着购买了该文档的版权，仅供个人/单位学习、研究之用，不得用于商业用途，未经授权，严禁复制、发行、汇编、翻译或者网络传播等，侵权必究。
- 3、本站所有内容均由合作方或网友上传，本站不对文档的完整性、权威性及其观点立场正确性做任何保证或承诺！文档内容仅供研究参考，付费前请自行鉴别。如您付费，意味着您自己接受本站规则且自行承担风险，本站不退款、不进行额外附加服务；查看《如何避免下载的几个坑》。如果您已付费下载过本站文档，您可以点击 这里二次下载。
- 4、如文档侵犯商业秘密、侵犯著作权、侵犯人身权等，请点击“版权申诉”（推荐），也可以打举报电话：400-050-0827(电话支持时间：9:00-18:30)。
- 5、该文档为VIP文档，如果想要下载，成为VIP会员后，下载免费。
- 6、成为VIP后，下载本文档将扣除1次下载权益。下载后，不支持退款、换文档。如有疑问请联系我们。
- 7、成为VIP后，您将拥有八大权益，权益包括：VIP文档下载权益、阅读免打扰、文档格式转换、高级专利检索、专属身份标志、高级客服、多端互通、版权登记。
- 8、VIP文档为合作方或网友上传，每下载1次， 网站将根据用户上传文档的质量评分、类型等，对文档贡献者给予高额补贴、流量扶持。如果你也想贡献VIP文档。上传文档
查看更多
Study on Hydrogen Permeation in DP and QP Grades of AHSS underCathodic Charging and Simulated Service … ·1 ·
Study on Hydrogen Permeation in DP and QP Grades of
AHSS under Cathodic Charging and Simulated Service
Conditions 1
1 1 1 2 1
Liu Qinglong , Venezuela Jeffrey , Zhang Mingxing , Zhou Qingjun , Atrens Andrej
(1. The University of Queensland, Division of Materials, School of Mining and Mechanical Engineering,
St. Lucia, 4072 Australia；
2. Baoshan Iron Steel Co., Ltd., Research Institute, Shanghai 201900, China)
Abstract The hydrogen permeation behaviour of DP and QP grades of advanced high strength steels was investigated
using the permeability experiments (1) under cathodic charging at different potentials in 0.1 M NaOH solution, (2) in 3%
NaCl solution at the free potential simulating the corrosion behaviour of non-galvanized steel in service and (3) at zinc
potential for the corrosion condition of the galvanized steel during actual service.Under cathodic charging at different
potentials in 0.1 M NaOH solution, hydrogen permeation decreased with less negative charging potential, reflected by lower
values of permeation rate and diffusion coefficient. At the most severe charging condition of –1.700 VHg/HgO in the 0.1 M
NaOH solution, the permeation rate for 1200 DP-GI steel was 1.53 µA/cm and for 980 QP steel was 0.492 µA/cm. The
values for 1200 DP-GI and 980 QP steels at the least severe charging condition of –1.100 VHg/HgO were 0.178 µA/cm and
0.111 µA/cm, respectively. The hydrogen permeation rate under simulated servic