Effect of MgO on melting and crystallization of CaO-Fe O system ·1 · 2 3 Effect of MgO on Melting and Crystallization of CaO-Fe O System 2 3 Guo Xingmin, Yang Nan (School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China) Abstract To solve some problems of sinter properties and slag performance existed on use of iron ores with high-Al O 2 3 content in blast furnace, a favour method is to add amount of MgO into sinter. In this work, effect of MgO on melting and crystalization of binding phase in high-basicity siner has been investigated by using TG-DSC and crystalizing test of CaO-Fe O system (molar ratio=1:1) combining X-ray diffraction and Scanning electron microscopy. The result showed 2 3 that MgO added into CaO-Fe2O3 system increases the initial melting temperature from the eutectic temperature of CaO⋅Fe O and CaO⋅2Fe O to the peritectic temperature of CaO⋅Fe O and 2CaO⋅Fe O in the heating process, 2 3 2 3 2 3 2 3 simultaneously the beginning temperature of crystallization of calcium ferrite increases with increase of MgO cont