Gemini表面活性剂在合成纳米乳液中的应用-AmazonS3.PDF

《化学通报》在线预览版 Gemini 表面活性剂在合成纳米乳液中的应用 ∗ 郭宝民, 王正武 , 姚柏龙，颜秀花 (江南大学 化学与材料学院， 无锡 214122) 摘要 本文以过硫酸铵为引发剂，通过种子微乳液聚合的方法研究了阴离子型 Gemini 表面活性剂（自制）在形成涂料 或胶粘剂用乳液的功能。研究发现阴离子型 Gemini 表面活性剂在微乳液聚合中是高效的乳化剂，可以提供典型的粒径控制 及良好的乳液稳定性，只需1%左右就可以得到固含量45%左右的透明纳米级丙烯酸乳液，并维持平均粒径在31nm左右。 关键词 微乳液聚合 Gemini 表面活性剂 Application of Gemini Surfactant in Micro-Emulsion Polymerization * Guo Baomin, Wang Zhengwu , Yao Bailong, Yan Xiuhua (School of Chemical and Material Engineering, Southern Yangtze University, Wuxi 214122) Abstract Function of Gemini emulsifiers (self-prepared) as anionic emulsifier in emulsion for coatings and adhesives is described by the process of seeded micro-emulsion polymerization initiated by the initiator ammonium persulfate (APS). It was found that Gemini emulsifiers are very effective in micro-emulsion polymerization, providing typical colloid particle size control, and excellent stability of the emulsion. With only about 1% content, high solid-content (about 40%) and small particle diameters (about 31nm) transparent copolymer latexes were attained. Key words Micro-emulsion polymerization, Gemini, Surfactants Gemini 表面活性剂是一种二聚表面活性剂，它是由两个双亲分子的离子头基经连接基团通过化学键连 结而成的，如图 1。Gemini 表面活性剂一般由两个疏水的烷基链和两个离子头基和一个连结基团构成。根 据离子头不同可分为阳离子型 Gemini 表面活性剂、阴离子型表面活性剂、非离子型表面活性剂和两性离 子型表面活性剂。与单体表面活性剂相比较，Gemini 表面活性剂具有很多优良性质。近几年，世界各国对 它的研究兴趣异常高涨，正逐渐成为国际胶体科学、相关领域和工业应用的研究热点。目前对 Gemini 的 介绍[1～5]，多以其分子结构和合成工作为主，而应用方面却很少涉及。Gemini 表面活性剂和单体表面活性 剂(尤其是非离子型表面活性剂)混合时，可以产生更强的协同效应。在通常的 O/W微乳聚合体系中，为了 溶解含量相对较低（＜10%）的单体，往往需要高的表面活性剂浓度（7%～15%），且体系中存在大量空胶 束[6～8]，大量的乳化剂的存在使涂膜的耐水性、致密性、附着力大大降低。因此必须寻找新的乳化体系， 降低乳化剂用量，提高单体含量。本文以 Gemini 表面活性剂代替传统活性剂，仅用 1%左右就可以获得固 含量为 45%的纳米级乳液，并对温度、