V、Ti合金化对玻璃模具材料抗氧化和耐热疲劳性影响.pdf

学兔兔 Ju1．2011 铸 造 VoI．60 NO．7 FOUNDRY ·697· V、Ti合金化对玻璃模具材料抗氧化 及耐热疲劳性的影响 吴进钱，黄新民，杨 明，韩和兵，曹钧力 (合肥工业大学材料科学与工程学院，安徽合肥230009) 摘要：通过测试不同v／Ti比条件下蠕墨铸铁玻璃模具材料的抗氧化及热疲劳性能，研究了蠕墨铸铁的钒、钛合金化工 艺，并探讨了影响这些性能的因素。结果表明，在V、Ti变化范围内，v／Ti比为1．63时蠕墨铸铁具有较均匀的铁素体基 体+蠕虫状石墨组织，以及良好的热物性。 关键词：蠕墨铸铁；玻璃模具材料；抗氧化；耐热疲劳 中图分类号：TG143．49 文献标识码：A 文章编号：1001—4977(201 1)07—0697—03 Effect of Vanadium and Titanium Alloying on Antioxidation and Thermal Fatigue Resistance of Glass Mold Material WU Jin-qian，HUANG Xin—min，YANG Ming，HAN He-bing，CAO Jun-li (School of Material Science and Technology of Hefei Institute of Technology， Hefei 230009，Anhui，China) Abstract：The antioxidation and thermaI fatigue resistance of vermicular graphite cast irons with different ratio of V厂ri were tested，which are the mold materials for glass forming．The technology of vanadium and titanium alloying was studied and the influencing factors on the properties were discussed．The results show that when the ratio of V／Ti iS 1．63．the vermicular graphite cast Iron has a more unifOrm structure of ferrite matrix+vermicular graphite。and good thermal properties． Key wOrdS：vermicular graphite cast iron；glass mold material；antioxidation；thermaI fatigue 在玻璃制品的成形过程中，模具频繁地接触I 100℃ 过控制铁液的出炉温度和浇注温度来控制铸铁的组织 以上的熔融玻璃，承受氧化、生长及热疲劳等作用。 形态，以获得蠕虫状石墨+铁素体基体组织，以提高模 模腔热平衡温度一般在450～650℃，长期处于高温状 具材料的高温热物性能，其试验材料化学成分见表1。 态下工作，而且在反复的开模、合模的过程中产生摩 表1 试验材料的化学成分 擦，因此要求玻璃模具应具有良好的耐热、耐磨、耐 Table 1 Chemical compositi