铸造温度对Zr53.9Cu29.4Ni4.9Al9.8Fe2块体金属玻璃力学性能和组织的影响.pdfVIP

Rare Metal Materials and Engineering Volume 41, Issue 11, November 2012 Online English edition of the Chinese language journal Cite this article as: Rare Metal Materials and Engineering, 2012, 41(11): 1891-1895. ARTICLE Effect of Casting Temperature on Mechanical Properties and Microstructure of Zr53.9Cu29.4Ni4.9Al9.8 Fe2 Bulk Metallic Glass 1,2 2 2 2 Liu Guangqiao , Kou Shengzhong , Li Chunyan , Zhao Yanchun 1 2 Lanzhou City University, Lanzhou 730070, China; State Key Laboratory of Gansu Advanced Non-ferrous Metal Materials, Lanzhou Uni- versity of Technology, Lanzhou 730050, China Abstract: Zr Cu Ni Al Fe alloy sample with the diameter of 3 mm was prepared by Cu mold suction casting at different 53.9 29.4 4.9 9.8 2 temperatures. The effect of casting temperature on mechanical properties and microstructure of the as-cast alloy was investigated. It is found that there is a critical casting temperature for the fully amorphous structure, below which the crystallization phase might be precipitated. Experiment results show that the compressive strength increases and the compressive plasticity slightly decreases when the casting temperature increases to certain extent. However, the compressive strength and the compressive plasticity simultaneously increase when the casting voltage increases to 9 kV, and the compressive plasticity is 2.62%. Mechanical properties of BMG can be tailored to certain extent by controlling the casting temperature, which is correlated with free volume and residual stresses. Key words: bulk metallic glass;