一种SiC陶瓷支架增强铸铁基复合材料的制备.pdfVIP

Rare Metal Materials and Engineering Volume 41, Suppl. 2, September 2012 Cite this article as: Rare Metal Materials and Engineering, 2012, 41(S2): 157-160. Preparation of a SiC Scaffold Reinforced Cast Iron Matrix Composite 1,2 1 1 2 3 3 Liu Guiwu , Wang Qian , Qiao Guanjun , Lu Tianjian , Li Lin , Wang Juan 1 State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, Xi’an 710049, China 2 MOE Key Laboratory for Strength and Vibration, Xi’an Jiaotong University, Xi’an 710049, China 3 Guangzhou Institute for Non-ferrous Metal Research, Guangzhou 510650, China Abstract: A novel route was developed to fabricate SiC scaffold reinforced cast iron matrix composite based on a series of processing techniques of materials. The interfacial behavior and wear property of the composite were also investigated. It is demonstrated that high quality SiC ceramic scaffolds could be obtained by effectively siliconizing the carbon preforms having hierarchical macropores, crosslinked network structure and high porosity. The presence of high content free silicon in the ceramic reinforcement and graphitizing and active elements (such as Fe and Cr) for SiC in the metal matrix lead to strong interfacial interactions, resulting in serious dissolution of SiC scaffold. Compared with wear resistance of the metal matrix, that of the composite can be obviously improved due to the addition of SiC scaffold. Key words: SiC ceramic; cast iron; metal-matrix composite; interfacia