超低温环境下导电混凝土除冰和其冻融循环性能研究.pdfVIP

学兔兔 2013年第l2期 混凝 土与水 泥制品 2013 No．12 l2月 CHINA CONCRETE AND CEMENT PRODUC rS December 超低温环境下导电混凝土除冰及其冻融循环性能研究 赵若红，钱 兴，傅继阳 (广州大学广东高校结构安全与健康监测工程技术研究中心， 广州市结构安全与健康监测重点实验室，510006) 摘 要：选用钢纤维和石墨作为导电混凝土导电相材料，通过室内常温条件下升温试验测试比较各配方的导 电性能，选取导电性能优良的试块，验证其在超低温-32℃条件下的融雪除冰性能。试验结果表明，质量比例2％钢 纤维加1．5％石墨所制备的导电混凝土试件融冰效果最好。该试件经历五次超低温冻融循环仍保持良好的除冰性 能。能够长期用于超低温除冰。 关键词：导电混凝土；除冰性能；超低温环境 Abstract： e steel fiber and graphite are used as conductive paste materials to pioduee the conductive concrete． The conductivity of conductive concrete with different mix proportion was tested under the condition of the indoor temper- ature by the elevated temperature test，and the snowmeh deicing performance of the specimens with better conductivity were tested at an ultra—low temperature of一32oC．The results show that山e conductivity concrete specimen with 2％steel fiber and 1．5％graphite has great snowmeh deicing performance，and after five deicing experiments，the specimen Can still keep good deicing performance，SO it Can be used on long—term deicing at low temperature． Key words：Conductive concrete；Deicing performance；Ultra-low temperature environment 中图分类号：TU375．4 文献标识码：A 文章编号：1000—4637(2013)12—41—03 0 前言 不同配比混凝土的除冰性能进行了比较。同时进行 自2003年美国内布拉斯加州道路管理局设计 了导电混凝土板的多次冻融循环试验。 完成了世界上首座导电混凝土融雪除冰的Roca 1 试件制备 Spur大桥后 it]．Christopher Y．Tuan教授等人用5年 1．1原材料 时间，基于该州条件进行了研究和观测团，成果受到 水泥为P·O 42．5级，容重3000kg／m。，3d抗压强 世界各国关注。此后多个国家开始了相关研究[31。国 度30．6MPa，初凝时间135min。砂为中砂，平均粒径 内导电混凝土方面的研究起步较晚，唐祖全教授等 0．25～0．5mm，占总质量50％砂的粒径≤0．25mm。石 人以碳纤维作为导电相材料做了大量的研究工作 为级配良