粉煤灰海工自密实高性能混凝土配合比参数试验研究.pdfVIP

学兔兔 2011年第8期 混 凝土与水泥制 品 20l1 N08 8月 CHINA CONCRETE AND CEMENT PRODUCTS August 粉煤灰海工自密实高性能混凝土 配合比参数的试验研究 王成启，张悦然 (中交上海三航科学研究院有限公司，200032) 摘 要：为满足海洋环境下混凝土的施工要求，开展了粉煤灰海工自密实高性能混凝土配合比参数的试验研 究。试验结果表明，掺入30％-40％粉煤灰、水胶比为0．35～0．37、用水量为170kg／m3的自密实混凝土具有较高的流动 性、填充性、间隙通过性和抗离析性，满足自密卖混凝土的施工要求，且具有较高的抗压强度和抗氯盐侵蚀性能，满 足海洋环境下抗氯盐侵蚀的耐久性要求。 关键词：粉煤灰；海工自密实高性能混凝土；流动性；填充性；间隙通过性；抗氯盐侵蚀 Abstract：To satisfy the marine concrete construction，the mix propo~ion parameters of fly ash high performance self-compacting marine concrete is experimentally studied．Experimental results show that the fluidity，filling ability，pass- ing ability and segregation resistance of self-compacting concrete with 30％—-40％ fly ash are better when its water—-binder ratio is from 0．35 to 0．37 and its water content is held at 1 70 kg／m0．which satisfies the demand of marine concrete con— struction．Moreover,its compressive strength and chloride resistance is higher and it can be used in concrete structure of marine circumstance． Key words：Fly ash；High performance self—compacting marine concrete；Fluidity；Filling ability；Passing ability； Chloride resistance 中图分类号：TU528 文献标识码：A 文章编号：1000—4637(2011)08—01—07 O 前言 煤灰可改善混凝土的工作性能和耐久性，是配制高 自密实混凝土(Self—Compacting Concrete，简称 性能混凝土的主要途径之一 。本文开展了自密实 SCC)，也有人称为高流态混凝土 (Highly Fluidized 混凝土配合比参数对海工自密实混凝土工作性能 Concrete)，是指混凝土无需振捣即可充满模板和包 的影响研究及其抗氯盐侵蚀耐久性的研究，以期配 裹钢筋，属于高性能混凝土【1-3]。之所以称其为高性 制出工作性能良好，且具有较高抗压强度和抗氯盐 能混凝土，是因为白密实混凝土具有很高的施工性 侵蚀性能的海工自密实高性能混凝土。 能，可不需人工振捣，减轻劳动强度。自密实混凝土 1 试验原材料 的自密实性能属拌合物施工性能，与混凝土强度和 1．1 水泥 所选材料的活性并没有