工艺因素对表面复合铸渗层质量的影响.pdfVIP

Vol.31 No. 8 # 1010 # FO NDRY TECHNOLOGY Aug.2010 王 莹 ( , 471023) : 采用传统铸渗工艺研究了工艺因素对表面复合铸渗层质量的影响, 结果表明: 适当的浇注 度有利于形成高质量的表 面复合铸渗层, 小型铸钢件的适宜浇注 度为1 650 ! ; 要形成与基体结合良好的复合铸渗层, 需有合适的涂层厚度,试验条 件下, 涂层厚度为5 mm 时的复合铸渗层质量较好; 涂层位于铸型侧面较位于铸型底部易于形成高质量的表面复合铸渗层 : 表面复合铸渗层; 浇注 度; 涂层厚度; 涂层位置 :TB331 : A : 2010) Inf luence of Process Fact ors on the Qualit y of Surface Composite Layer WANGYing (Department of Civil Engineering, Luoyang Institute of Science an Technology, Luoyang 471023, China) Abstract: The influence of process factors on t he quality of surface composite layer is researched wit h convent ional castpenetrating process. The result indicates that t he highquality surface composite layer is prone to get when pouring temperat ure is suitable and t he suitable pouring temperature is 1 650 ! for little cast steel. Appropriate thickness of coat ing layer is benef it to get surface composite layer with high quality and t he quality of sample wit h 5mm coating layer is better than other samples in test . surface composite layer with high quality is easy to obtain when coating layer is located in the side of foundry mould. Key words: Surface composite layer Pouring temperat ure Coat ing layer t hickness Coat ing layer position ,, ,, , , , 200 ! , 2 h ZG230 [ 1~ 3] 450, , [4] , , , [5] , , 900∀ 10 ! , 2 h , 2 2. 1 浇注 度对表面复合铸渗层质量的影响 1 , , 158016501720 ! 3 , ,