汽化冷却技术在武钢二热轧加热炉应用及改进.pdf

工业炉窑热工 汽化冷却技术在武钢二热轧加热炉应用及改进 曹炳雷 赵利红 （武汉钢铁集团公司热轧厂 湖北武汉 430080 ） 摘 要：分析了武钢二热轧加热炉汽化冷却系统存在的主要问题，在此基础上提出了相应的改进措施，并将这些措施逐步 实施。生产实践表明，改进后的冷却系统既保证了冷却效果，又降低了水消耗，同时又改善了水梁结垢状态，延长了水梁 寿命，提高了炉子效率。 关键词：汽化冷却；强制循环；软水；除氧；旋转接头 Application and Improvement of Vaporization Cooling Technology in Walking Beam Furnace of HSM2 in WISCO CAO Bing-lei ZHAO Li-hong (Wuhan iron steel(group) Co., HSM, Wuhan, Hubei, 430080, China) Abstract: Vaporization cooling technology has been applied in HSM2 heating furnaces in WISCO, but there were some problems in the vaporization cooling system. The key problems were analyzed firstly, and then the corresponding solving measures were brought forth. Moreover, the measures were carried out in the vaporization cooling system of in HSM2 heating furnaces. Through the practice, the improved cooling system has the following advantage, such as better cooling effect, lower water consumption, thinner furring, longer life, higher efficiency etc. Key word: Vaporization cooling; Circulation; Soft water; Deoxygenization; Rotate joint 次，给二热轧生产和正常的轧线调试造成不利影 1 引言 响。每次停炉造成大量的软水和煤气浪费，系统 加热炉步进梁的冷却方式经历了由工业水直 内 70 余吨软水被放掉，停炉降温及升温烘炉也消 流敞开循环到强制循环汽化冷却，实现了软水闭 耗不少煤气。为了解决各类故障，我们各专业人 路循环，这一演进过程体现了冷却技术的发展。 员及设计院联合诊断，经过近 3 年的摸索，最终 汽化冷却系统由两大部分组成：循环系统和给水 在其运行维护和操作上形成了一套有效的方法， 除氧系统。由于其采用经化学处理的除氧软水为 保证了汽化冷却系统的稳定运行，真正发挥了其 冷却介质，排除了水管中结垢的可能性；大幅提 优势。以下分几个方面谈谈我们所做的改进工作。 高水温并利用水的汽化潜热，其产生的蒸汽可以 2 循环系统存在问题及解决方法 二次利用，降低了加热炉能耗且减少了水的消耗， 提高了炉子的热效率和延长了水梁的寿命，使加 2.1 流程介绍及主要设备 热炉生产的经济性大为提高。 但是汽化冷却系统较传统冷却系统复杂，其 循环系统是将系统内的软水在 2.5MP