浅谈混凝土施工质量控制 222 浅谈混凝土施工质量控制 来源：中国论文下载中心 [ 09-11-06 14:11:00 ] 作者：徐泰钤 编辑：studa090420 【摘要】在我国工程建设领域中，钢筋混凝土结构以其造价低、设计理论成熟、施工技术成熟、抗震性能良好等优点占有绝对的比重。在水利水电工程、桥梁工程等土木工程领域发挥着极其重要作用。但是混凝土材料品质及配合比质量的波动以及混凝土输送、浇筑、养护等施工工艺对混凝土质量有较大的影响，施工过程中需要严格的质量控制。 【关键词】混凝土；原材料控制；拌制；运输；浇筑；养护；拆模；冬季混凝土施工 【Abstract】In construction field in China, the reinforced concrete structure with its low cost, sophisticated design theory, construction technology is mature, the advantages of seismic performance of good possession of the absolute proportion. In the water conservancy and hydropower engineering, bridge engineering, civil engineering is playing an extremely important role. However, the quality and mix proportion of concrete materials, fluctuating as well as the quality of concrete transport, pouring, maintenance and so the quality of concrete construction technology have a greater impact of the construction process requires strict quality control. 【Key words】Concrete; Raw material control; Mixing; Transport; Pouring concrete; Conservation; Form removal; Winter concrete construction 1. 原材料控制 普通混凝土是由水泥、水、细骨料、化学外加剂、矿物质混合材料，按比例配合，经过均匀拌制，振捣密实成型及养护硬化而成的人工石材。 1.1水泥。水泥有多种品种、标号应根据设计图纸的要求的要求和实际使用部位的环境条件，选择适当的水泥品种和标号。高强混凝土应优先选择高标号水泥进行试配。 1.2砂。细骨料砂，要重点检查其质地、级配、细度模数、含泥量和有害物质含量。其重点是含泥量和有害物质含量。这两项对于混凝土强度的影响较大。用于拌制混凝土的细度模数应在3.7-1.6之间。结构用砂含泥量一般不应超过3%，有害物用质（云母、有机物、硫酸盐等）含量不应超过2%。 1.3石子。粗骨料石子，应重点检查其质地、级配、针片状颗粒含量、含量泥量及最大粒径。一般采用1cm-3cm的碎石，卵石一般能用于结构受力部位，严禁混有煅烧过的石灰石块或白云石块。 1.4水。凡是不能饮用的水，应在水质化验和抗腐蚀试验合格后，方可用于拌制混凝土。污水、工业废水、PH值小于4的酸性水和硫酸盐含量超过水重1%的水，不能用于拌制混凝土。对预应力混凝土的施工用水，更样着重控制。 1.5外加剂。首先，应检查外加剂生产厂家的生产许可证，质量保证料和有相应资质的检测单位出具的性能试验报告。其次，在混凝土外加剂使用前，应进行试配并进行试验检验，以复验混凝土外加剂与工程所有水泥是否相适应，以及是否满足施工要求的混凝土性能和有关设计要求指示（如坑渗标号等）。另外，应注意混凝土外加剂使用说明的有效日期、防止过期失效的外加剂用于工程。同时，要严格控制剂量，不得随意添加，在搅拌混凝土时，掺加外加剂的混凝土搅拌时间应适当延长。应大力推广使用新型的复合型混凝土外加剂，以适应先进的施工工艺的多种要求。 2. 配合比的质量控制 混凝土应根据实际采用的原材料进行配合比设计，并按普通混凝土拌和物性能试验方法等标准进行试验、试配，以满足混凝土强度、耐久性和工作性能（坍落度等）的要求，不得采用经验配合比。同时，应符合经济、合理的原则。混凝土生