冷却速度对镍基合金堆焊层焊接热裂纹的影响-Read.PDFVIP

　第 12 卷第 2 期　　　　　　　　　　材　料　开　发　与　应　用　　　　　　　　　　1997 年 4 月　 应用研究 冷却速度对镍基合金堆焊层焊接热裂纹的影响 上海交通大学　姚寿山　陆　皓　朱燕萍 上海锅炉厂　　牛明安　张茂荣　　　　 摘 要 采用托马斯镶嵌块试样和中子测量管与封头堆焊层的实样进行焊接试验, 比较了空冷、水冷 和- 40 ℃干冰酒精冷却条件下焊接对焊缝微裂纹的影响。结果表明焊缝的高速冷却有利于镍基合 金焊缝热裂纹的减少。 关键词: 镍基合金　焊接　热裂纹 Inf luence of Cooling Ra te on Hot Crack ing - in Bead W eld ing Layers of N i ba se A lloys 　 　 Yao Shou shan L u H ao Zhu Yanp ing (Shanghai J iao tong U n iversity) N iu M ingan　Zhang M ao rong (Shanghai Bo iler W o rk s) Abstract: W elding tests w ere m ade by using Tom as mo saic block samp les and actural samp les taken from bead w elding layers betw een new tron m easuring tube and dom e of a p ressure hull in a nuclear pow er station. T he w eld crack s under different coo ling conditons are compared, including , - 40℃. air coo ling w ater coo ling and dry ice coo ling at T he results show that a h igher coo ling . rate fo r a w eld is benifit fo r the decrease of ho t crack s in N i base alloy w elds : - 　 　 Key words N i ba se a lloy W eld ing Hot crack 文。 1　前言 而且核电站的主要设备压力壳、蒸汽发生器 和稳压器还存在着接管与安全端异种钢焊接 　　核电站不但存在低合金钢的焊接问题, 问题, 即带有不锈钢堆焊层的低合金钢与不 锈钢或镍基合金之间的焊接 问题, 如我 国 ’96 船舶材料科学与工程学术交流会交流论 “728 ”秦山核电站的蒸汽发生器和稳压器的 ·2 · © 1994-2008 China Academ