截齿表面感应熔覆WC增强Fe基熔覆层的研究.pdfVIP

截齿表面感应熔覆WC增强Fe基熔覆层的研究 杨会龙。孙玉福。赵靖字，马永华，王刘利。肖志云。王璐。丁丽平 (郑州大学材料科学与工程学院，郑州450002) [摘要]采用高频感应熔覆技术在采煤机截齿前端表面制备高耐磨的WC增强Fe基熔覆层，结果表明： Fe。C等组成，熔覆层厚度约2trim，硬度达63．6HRC，显微硬度平均值为1007．9HV0．3，耐磨性为基体的4．06 倍，耐磨性优异。 [关键词]高频感应熔覆；截齿；WC；Fe基熔覆层；耐磨性 [中图分类号]TGl74．42 [文献标识码]A ontheFe-BasedReinforcedWC Study Coating by on PickSurfaceFormed Induction Cutting byHighFrequency Cladding YANG Hui—long，SUNYu-fu，ZHAOding-yu，MAYong-hua， WANGLiu-li，XIAO Lu，DING Zhi-yun，WANG Li-ping (Sch001ofMaterialsScienceand 450002，China) Engineering，ZhengzhouUniversity，Zhengzhou AFe—based reinforcedWCof wearresistancewasfabricatedonthe surface by pick [Abstract] coating high cutting resultsshow bondisattainedbetweenthe InductionCladding(HFIC)，Thethat：a byHighFrequency metallurgical Of eutecticcarbideandlittle themain andthesubstrate，the WC，aM coating coatingcomprisesaustenite，herringbone and C mm ofthe C eta1．The isabout2 thickness，andthe phases coatingare(Cr，Fe)7C3，WC，Fe3W3 Fe3 coating rockwellhardnessreaches63．6HRC，themicrohardnessis1007．9HV0．3，andthewearresistance0fthecoat— average is timesOfthe excellentwearresistance． ing 4．06 substrate，showing induction resistance