不同填充物对机械法制纤维素缓冲包装材料性能的影响研究.pdfVIP

不同填充物对机械法制纤维素缓冲包装材料性能的影响 1 1 2 赵红 麒麟 李洪来 1 （齐齐哈尔大学轻工纺织学院包装教研室，黑龙江齐齐哈尔，161006） 2 （陕西科技大学造纸工程学院，陕西西安，710021） 摘 要：针对机械法制备纤维素发泡缓冲材料密度小、强度低的特点，对其加入填充物后的性能进行了较 为详细的研究。研究表明加入适量的填充物是必需的，而且不同的填充物对发泡体性能的影响也有所不同。。 关键词：纤维素；发泡；填充物；静态压缩 The Factors Study of the Buffering and Packing Material of Fiber by Machine Foam 1 1 2 ZHAO Hong , QI Lin , Li Honglai 1 ( Qiqihar University, Qiqihar 161006 , China) 2 ( Shaanxi University of Science and Technology, School of Paper Making Engineering, Xian 710021) Abstract: The performance of the filler addition to the cellulose foam buffering material was investigated according to its low density and low strength that prepared by mechanical method. The results showed that the addition of appropriate amount of filler into the cellulose foam buffering material was necessary and the effects of different filler on the performance of the foam were different. Keywords: fiber; forming; filling: static compression 目前在家用电器、精密仪器、电子计算机、电子元器件等包装中大量使用的聚苯乙烯 (EPS)类发泡缓冲包装材料，是一种高分子化学合成物，其包装废弃物，不能自然降解和完 全回收。随着全球贸易的一体化及各国对环境问题的高度重视，这些不能自然降解和回收利 [1-2] 用的缓冲包装材料的应用将受到越来越大的限制，最终将被淘汰 。 纤维素纤维缓冲包装材料具有很好生物可降解性、环境协调性，它能完全降解腐烂因而 其废弃物不会对环境造成污染。而且纤维素纤维发泡材料以其生产工艺简单，生产时间及周 [3-4] 期短，能耗和原料成本低，防静电、防腐蚀性等特点成为世界各国竞相研究和开发的热点 。 由于机械法制备的纤维素发泡缓冲材料密度较小，所以纤维之间的孔隙较大，虽然纤维 之间会有氢键和其它次价键的形成，但是整个发泡体的强度还是比较小，需要加入强度补强 物质。而且由于泡沫体系的不稳定性，在烘干的过程中，泡沫体系难免塌陷，所以加入填充 物是必要的，而且填充物的加入大大的降低了纤维用量，降低了发泡体的制备成本。 1 试验 1.1 试验原料仪器和设备 漂白针叶木浆，明胶（生化试剂）、发泡剂（醚类，化学纯），甲基纤维