电泳显示用双层微胶囊的制备研究.pdfVIP

电泳显示用双层微胶囊的制备 * 谢建宇，冯亚青 ，王静，李祥高，周康 (天津大学化工学院，天津300072，中国) 摘 要：用尿素－甲醛原位聚合法与明胶-阿拉伯胶复凝聚法相结合制备了电泳显示用双层微胶囊。考察了系 统调节剂、pH值和加醛方式对单层微胶囊形貌的影响，以及双层微胶囊与单层微胶囊在干燥过程中的破损 率。实验结果表明，以明胶为系统调节剂，pH值为3.0 ～3.5，采用滴加方式加入甲醛制备的单层脲醛树脂微 胶囊，囊壁透明、光滑，球形度好；包覆明胶后制备的双层微胶囊，壁材强度和韧性有显著提高。 关键词：电泳显示；原位聚合；复凝聚；双层微胶囊 Preparation of Double Layered Microcapsule for Electrophoretic Display * XIE Jian-yu ，FENG Ya-qing ，WANG Jing ，LI Xiang-gao ，ZHOU Kang ( School of Chemical Engineering and Technology ，Tianjin University，Tianjin 300072，China) Abstract ：Double layered microcapsules for electrophoretic display were prepared by in situ polymerization of urea-formaldehyde and complex coacervation of gelatin-gum Arabic. The paper investigated the effects of system modifier, pH value, the method of adding formaldehyde and broken rates of monolayer microcapsules and double layered microcapsules in dry process. When gelatin was used as system modifier, the pH value was sustained between 3.0 and 3.5, and dropping the formaldehyde, the monolayer microcapsules with good transparence and sphericity could be obtained. When microcapsules were encapsulated by gelatin, the strength and flexibility of wall were improved. Keywords ：electrophoretic display ；in situ polymerization ；complex coacervation ； double layered microcapsules 随着计算机技术的发展和因特网的普及，通过计算机等媒介浏览“电子出版物”已经成 为一种新的阅读方式。但传统的显像管(CRT)显示，因其物理构造限制了向更大屏幕超薄方 向的发展，从而逐渐被液晶显示（LCD）、等离子体显示（PDP）等所取代。但这些方式还是 存在亮度、对比度、视角、色纯度等问题。1997 年美国 E-Ink 公司发展了一种电泳粒子微胶 囊显示技术 【1】 ，由于这类显示器利用微粒的双稳态实现显示，并具有纸的柔软性，且对比度 好、可视角度大、不需背景光源，因此引起人们极大的关注。 微胶囊是电子墨水显示的核心部分，采用微胶囊技术，将带电粒子包裹在微胶囊内，克 收稿日期：2006-08-22 基金项目：国家 863 计划资助项目(No.2004AA302010) 作者简介：谢建宇，1977，博士研究生，xjy2001@ 服了电泳图像显示中颗粒在大尺度范围内容