轴承钢中镁铝合金对夹杂物变性的研究.pdfVIP

第十五届全国炼钢学术会议文集 轴承钢中镁铝合金对夹杂物变性的研究 龚伟 姜周华 王博 王文忠 （东北大学材料与冶金学院） 摘要 采用三种不同镁含量的镁铝合金对轴承钢钢液进行处理，得到钢中全氧含量、夹杂物形态、尺寸、数 量的检测结果，同时考察了含镁合金对轴承钢碳化物的球化作用。实验结果表明，镁铝合金处理钢液后夹杂 物成分以镁铝尖晶石为主，观察镁铝合金处理实验终点样，溶解在轴承钢中的镁元素起到了球化碳化物的作 用，并且随着镁铝合金中镁含量的增加，这种效果越明显。 关键词 轴承钢 镁 夹杂物 碳化物 Study on effect of magnesium aluminum alloy to inclusion in bearing steel GONG Wei JIANG Zhouhua WANG Bo WANG Wenzhong (School of Materials and Metallurgy, Northeastern University) ABSTRACT Three different content magnesium aluminum alloys has been used in bearing steel, then the test result of the total oxygen content of, the shape, amount and size of inclusions in bearing steel was gained, and the spheroidizing of magnesium alloy to carbide in bearing steel was checked at the same time. The result shows that the main content of inclusion is spinel after treating with magnesium aluminum alloy. And the samples of the ingots at the terminal have been observed, the result confirms the conclusion that the sphericalization is more obvious when Al-Mg alloy with higher magnesium content is used. KEY WORDS Bearing steel, magnesium, inclusion, carbide 1 前言 目前电炉生产轴承钢工艺是以Al作为主要脱氧剂的，用Al脱氧可以获得很低的溶解氧含量，如果脱氧 产物Al O 脱除充分，就可以获得洁净度很高的钢液。虽然Al O 夹杂物与钢液润湿角小、上浮速度快，但 2 3 2 3 [1] 是仍会有大量的Al O 颗粒残留在钢液中聚集成团簇状的Al O 群 。这些团簇状的Al O 群对轴承钢的疲劳 2 3 2 3 2 3 寿命有害，并且在浇注过程中易堵塞水口。因此，对残留在钢中的Al O 夹杂物进行变性处理以消除其危害 2 3 是提高轴承钢疲劳寿命的有效途径。 如果将钢中溶解的镁含量提高，镁参与脱氧反应生成的氧化镁