双电极阳极氧化制备TiO2纳米管外加电压的影响机理研究.pdf

双电极阳极氧化制备TiO 纳米管外加电压的影响机理 2 陈粤，赵洪彬，崔国峰，刘鸿，吕树申* (中山大学化学与化工学院，广州510275) 摘要：本文采用电化学阳极氧化法，通过调节阳极氧化电压，得到管径可控的TiO2 纳米管阵列，并通过分 析电流密度讨论纳米管生长过程。通过实验比较，指出双电极阳极氧化体系溶液压降（IR drop ）对纳米管 制备的影响。通过讨论初始孔核的竞争氧化，提出阳极氧化电压优化管径大小的机理模型。 关键词：阳极氧化；TiO2 纳米管；双电极体系；电压影响 Mechanism Investigation on the Effect of Anodization Voltage on TiO2 Nanotube Diameter Formed in two-electrode configuration * CHEN Yue, ZHAO Hongbin, CUI Guofeng, LIU Hong, LU Shushen (School of Chemistry and Chemical Engineering, Sun Yat-sen University, Guangzhou 510275, Guangdong, China) Abstract: In this paper, the diameter of TiO nanotube arrays, formed by anodization, is tailored 2 by adjusting the anodization voltage. By analyzing the anodizing current transients, the growth mechanism is discussed. The effect of system IR drop on the fabrication has been evaluated by comparing the experimental results. A mechanism model is proposed to elucidate how the voltage optimized the diameter of the nanotubes by discussing the oxidizing competition between initial tube cores. Key words: anodization; TiO2 nanotube; two-electrode configuration; voltage 引 言： [1] [2] TiO2 在紫外光照射之下具有独特的光催化特性，其在光解水制氢 、超亲水材料 、沸 腾热界面材料[3]等领域具有潜在的应用。纳米形貌 TiO2 由于具有较高的比表面积，再加上 纳米尺寸的量子效应，表现出更多、更优越的性能。在染料敏化太阳能电池[4]、锂离子电池 [5] [6] [7] 、气敏器件 以及电致变色材料 等领域的应用均有所报道。纳米材料形貌结构对其性能 有重要的影响，因此，探索各种 TiO2 纳米材料制备方法以及控制其形貌是近年来的研究热 [8, 9] 点之一 。 通过电化学阳极氧化法可在 Ti 金属基底上制备规整的 TiO2 纳米管阵列。1999 年， *通讯联系人：E-mail: lvshsh@mail.sysu.edu.cn; Tel.: 020 基金项目：中山大学后备重点课题项目资助（31000-113