摘 要 以再生聚醚、TDI（甲苯二异氰酸酯repolymer was prepared with regenerated polyether and TDI?as main materials by the way of prepolymerization. Then one/two-component PU adhesive was made by adding different auxiliaries, respectively?.The effects of types and the dosage?of materials on the performance of the adhesive were discussed. The best performance of the adhesive which can be exerted was gained after testing the properties of viscosity, curing time,tensile strength and elongation etc. The results indicated that the properties of prepolymer were best when the mass ratio of the materials was set as follow： T280:220∶TDI∶chlorcosane?∶DBP = 34 ∶34∶17∶7.5∶7.5 .???Compare to the adhesive which was prepared by available formulation, one-component PU adhesive had faster curing speed,grater strength, good abrasive resistance and low cost which was cut by 19.7%. While two-component PU adhesive also had faster curing speed, grater hardness and strength, though the flexibility dropped a little. But the combination property was good as a whole , and the cost was cut by 25.8%. Key words: Regenerated Polyether Prepolymer One/two-component PU adhesive Cost 目 录 摘 要 I Abstract II 目 录 III 1 前言 1 1.1 分类 1 1.2 合成方法 2 1.3 应用 2 1.3.1汽车用聚氨酯胶粘剂 2 1.3.2木材用聚氨酯胶粘剂 3 1.3.3鞋用聚氨酯胶粘剂 3 1.3.4包装用聚氨酯胶粘剂 3 1.3.5建筑用聚氨酯胶粘剂 3 1.3.6油墨用聚氨酯胶粘剂 4 1.3.7其它方面 4 1.4 研究进展 4 1.5 选题意义 5 2 实验材料与方法 6 2.1 实验仪器 6 2.2 实验药品 6 2.3 实验原理 7 2.3.1聚氨酯结构特征 7 2.3.2再生聚醚结构特点 7 2.3.3 TDI结构特点 8 2.3.4实验基本原理 8 2.3.5产品性能的影响因素 9 2.4 实验方法 9 2.4.1单组分 PU胶粘剂的研制 9 2.4.2双组分PU胶粘剂的研制 11 2.4.3分析与测试[27] 12 3 结果与讨论 14 3.1 单组分PU胶粘剂的研制结果 14 3.2 双组分PU胶粘剂的研制结果 19 3.3 实验操作对结果的影响 22 3.3.1杂质的影响 22 3.3.2 反应时间与温度的影响 23 3.3.3加料顺序的影响 23 4 结论与展望 23 4.1 结论 23 4.2 展望 23 体会与致谢 24 参考文献 25 1 前言 聚氨酯胶粘剂是指在分子链中含有氨基甲酸酯基团（－NHCOO－）或异氰酸酯基（－NCO）的胶粘剂。聚氨酯胶粘剂是目前正在迅猛发展的聚氨酯树脂中的一个重要组成部分，具有优异性能，在许多方面都得到了广泛的应用，是八大合成胶粘剂中的重要品种之一聚氨酯胶粘剂20世纪40年代在德国工业化开发出类型品种，其化学基础研究和技术[6]单组分聚氨酯胶粘剂使用时不需要进行化学计量，也不需要添加其他的交联剂，只利用空气或基材表面的水分就可以固化，产生粘接作用，给操作者带来了极大的方便，目前应用比较广泛，在某些领域具有其他胶粘剂所无法替代的优势。如汽车